ABSTRACT
Multi-criteria decision-making (MCDM) methods have been widely used among researchers to provide a trade-off solution between best and worst, considering conflicting criteria and sets of preferences. An efficient and systematic literature review of these methods is needed to maintain their application in distinctive domains. To this end, this paper presents a comprehensive and systematic literature survey on "multi-objective optimization by ratio analysis" (MOORA) method and its fuzzy extensions developed and discussed in recent years. This review includes articles categorized based on the publication name, publishing year, journal name, type of applications, and type of fuzzy extensions. In addition, this review will enhance the understanding of practitioners and decision-makers on the MOORA method, its development, fuzzy hybridization, different application areas, and future work. The study revealed that the MOORA technique was predominantly used with the TOPSIS approach, followed by the AHP and COPRAS methods. Furthermore, 76.28 % use single and hybridization approaches among all MOORA studies, while 23.72 % use MOORA in a fuzzy environment.
ABSTRACT
Diglycidyl ether bisphenol A (DGEBA) is a thermosetting polymer with excellent cross-linking properties and an irreversible network structure that forms polymer chains when chemically reacting with hardeners such as amines and anhydrides. The resulting compound has exceptional thermomechanical and structural properties. The properties of the final compound are heavily influenced by cross-linking and network structure. In the present research, molecular dynamics (MD) simulations were used to investigate the mechanical properties of chemically cross-linked DGEBA and the curing agent diethyl toluene diamine (DETDA). The MD simulation was used to perform the cross-linking, and a comprehensive study on the mechanical properties of DGEBA/DETDA was conducted. To investigate the mechanical properties, the developed model was reinforced with hexagonal boron nitride nanosheet (h-BNNS) at various weight percentages (wt.%). The results showed that the density of the neat DGEBA/DETDA increases with increasing cross-linking. It is 1.13 g/cm3 at 90% cross-linking. Almost all cross-linking densities of neat DGEBA/DETDA had higher mechanical properties. At room temperature (300 K), the elastic modulus increases from 2.58 to 2.98 GPa for cross-linking densities of 80% (EP80), 85% (EP85), and 90% (EP90). The elastic modulus of EP85 and EP90 is 3% lower and 9% higher than the experimental value (2.71 GPa), respectively. In almost all cross-linking densities, the elastic modulus of the h-BNNS reinforced DGEBA/DETDA increases with the weight percentage (wt%) of the h-BNNS. Shear and bulk modulus increase when h-BNNS is added to the DGEBA/DETDA matrix.