1.
Nanoscale ; 7(7): 3263-9, 2015 Feb 21.
Article in English | MEDLINE | ID: mdl-25619890

ABSTRACT

We investigate, using scanning tunnelling microscopy, the adsorption of pentacene on Ni(111) at room temperature and the behaviour of these monolayer films with annealing up to 700 °C. We observe the conversion of pentacene into graphene, which begins from as low as 220 °C with the coalescence of pentacene molecules into large planar aggregates. Then, by annealing at 350 °C for 20 minutes, these aggregates expand into irregular domains of graphene tens of nanometers in size. On surfaces where graphene and nickel carbide coexist, pentacene shows preferential adsorption on the nickel carbide phase. The same pentacene to graphene transformation was also achieved on Cu(111), but at a higher activation temperature, producing large graphene domains that exhibit a range of moiré superlattice periodicities.

2.
Chem Commun (Camb) ; 50(63): 8791-3, 2014 Aug 14.
Article in English | MEDLINE | ID: mdl-24967741

ABSTRACT

The tip of a scanning tunneling microscope (STM) can be used to dehydrogenate freely-diffusing tetrathienoanthracene (TTA) molecules on Cu(111), trapping the molecules into metal-coordinated oligomeric structures. The process proceeds at bias voltages above ~3 V and produces organometallic structures identical to those resulting from the thermally-activated cross-coupling of a halogenated analogue. The process appears to be substrate dependent: no oligomerization was observed on Ag(111) or HOPG. This approach demonstrates the possibility of controlled synthesis and nanoscale patterning of 2D oligomer structures on selected surfaces.