Calorimetric Heats of Intrusion of LiCl Aqueous Solutions in Hydrophobic MFI-Type Zeosil: Influence of the Concentration.

For the first time, we report calorimetric measurements of intrusion of aqueous LiCl solutions in a hydrophobic pure siliceous MFI zeolite (silicalite-1) under high pressure. Our results show that the intrusion heats are strongly dependent on the LiCl concentration. The intrusion process is endothermic for diluted solutions (molar H2O/LiCl = 12) as well as for water, but it becomes exothermic for a concentration close to saturation (molar H2O/LiCl = 4). Analysis of the data in the framework of wetting thermodynamics shows that besides surface wetting, other phenomena occur during intrusion, such as hydrogen-bond weakening and composition change. In all cases, water is preferentially intruded so that the intruded phase becomes more diluted than the bulk solution. In the case of the most diluted solution, only water molecules seemed to be intruded. Furthermore, silicalite-1 is shown to be very stable in the presence of LiCl solution, with no noticeable structural and textural modifications observed after intrusion.

The functionalization of nanodiamonds (diamondoids) as a key parameter of their easily controlled self-assembly in micro- and nanocrystals from the vapor phase.

We detail herein readily accessible processes to control previously unobserved robust self-assemblies of nanodiamonds (diamondoids) in micro- and nanocrystals from their mild vapor deposition. The chemical functionalization of uniform and discernible nanodiamonds was found to be a key parameter, and depending on the type of functional group (hydroxy, fluorine, etc.) and its position on the diamondoid, the structure of the discrete deposits can vary dramatically. Thus, well-defined anisotropic structures such as rod, needle, triangle or truncated octahedron shapes can be obtained, and self-assembled edifices of sizes ranging from 20 nm to several hundred micrometers formed with conservation of a similar structure for a given diamondoid. Key thermodynamic data including sublimation enthalpy of diamondoid derivatives are reported, and the SEM of the self-assemblies coupled with EDX analyses and XRD attest the nature and purity of nanodiamond crystal deposits. This attractive method is simple and outperforms in terms of deposit quality dip-coating methods we used. This vapor phase deposition approach is expected to allow for an easy formation of diamondoid nanoobjects on different types of substrates.