ABSTRACT
This paper discusses the mechanical and physicochemical properties of film matrices based on chitosan, as well as the possibility of optimizing these properties by adding chitin nanofibrils. It is shown that with the introduction of chitin nanofibrils as a filler, the mechanical stability of the composite materials increases. By varying the concentration of chitin nanofibrils, it is possible to obtain a spectrum of samples with different bioactive properties for the growth of human dermal fibroblasts. Film matrices based on the nanocomposite of chitosan and 5 wt % chitin nanofibrils have an optimal balance of mechanical and physicochemical properties and bioactivity in relation to the culture of human dermal fibroblasts.
ABSTRACT
Electrical conductivity, surface tension and viscosity of chitosan-based composite nanofibers are reported. 20â¯wt.% of chitin nanofibrils introduced into a chitosan solution leads to increase in viscosity of the mixture; the effect of shear rate becomes more pronounced. This phenomenon is caused by the formation of cluster structures involving filler particles, and by orientation of chitin nanofibrils under the action of shear stresses in electromagnetic field. Presence of chitin facilitated formation of nanofibers in electric field and led to significant decrease in the amount of defects.
ABSTRACT
Biocompatible and bioresorbable composite fibers consisting of chitosan filled with anisotropic chitin nanofibrils with the length of 600-800 nm and cross section of about 11-12 nm as revealed by SEM and XRD were prepared by coagulation. Both chitin and chitosan components of the composite fibers displayed preferred orientations. Orientation of chitosan molecules induced by chitin nanocrystallites was confirmed by molecular modeling. The incorporation of 0.1-0.3 wt.% of chitin nanofibrils into chitosan matrix led to an increase in strength and Young modulus of the composite fibers.