ABSTRACT
Because of their high electrical conductivity CoSi2 nanostructures are potential candidates for preparing ordered nano-arrays to be used as electrode interconnectors and contacts in microelectronic devices. We here describe a controlled procedure for the endotaxial growth of hexagonal CoSi2 nanoplatelets buried in differently oriented single crystalline Si wafers on which a Co-doped SiO2 thin film was previously deposited. These nanomaterials were obtained by a clean procedure consisting of isothermal annealing at 750 °C under a He atmosphere of Co-doped SiO2 thin films deposited onto the surface of three differently oriented flat Si substrates, namely Si(001), Si(011) and Si(111). Buried CoSi2 nanoplatelets are in all cases spontaneously formed as a consequence of the diffusion of Co atoms into the silicon wafer and their reaction with host Si atoms. Our TEM and GISAXS analyses demonstrated that these arrays, irrespective of host Si orientation, consist of CoSi2 hexagonal nanoplatelets in all cases parallel to Si{111} crystallographic planes. Additionally, the dimensions of the nanoplatelets were consistently determined by TEM and GISAXS for the three different host Si single crystal orientations.
ABSTRACT
Silver nanodots and nanoripples have been grown on nanocavity-patterned polycrystalline Au templates by controlled electrodeposition. The initial step is the growth of a first continuous Ag monolayer followed by preferential deposition at nanocavities. The Ag-coated nanocavities act as preferred sites for instantaneous nucleation and growth of the three-dimensional metallic centres. By controlling the amount of deposited Ag, dots of approximately 50 nm average size and approximately 4 nm average height can be grown with spatial and size distributions dictated by the template. The dots are in a metastable state. Further Ag deposition drives the dot surface structure to nanoripple formation. Results show that electrodeposition on nanopatterned electrodes can be used to prepare a high density of nanostructures with a narrow size distribution and spatial order.