ABSTRACT
The magnetic properties of layered hydroxylammonium fluorocobaltate (NH(3)OH)(2)CoF(4) were investigated by measuring its dc magnetic susceptibility in zero-field-cooled (ZFC) and field-cooled (FC) regimes, its frequency dependent ac susceptibility, its isothermal magnetization curves after ZFC and FC regimes, and its heat capacity. Effects of pressure and magnetic field on magnetic phase transitions were studied by susceptibility and heat capacity measurements, respectively. The system undergoes a magnetic phase transition from a paramagnetic state to a canted antiferromagnetic state exhibiting a weak ferromagnetic behavior at T(C) = 46.5 K and an antiferromagnetic transition at T(N) = 2.9 K. The most spectacular manifestation of the complex magnetic behavior in this system is a shift of the isothermal magnetization hysteresis loop in a temperature range below 20 K after the FC regime-an exchange bias phenomenon. We investigated the exchange bias as a function of the magnetic field during cooling and as a function of temperature. The observed exchange bias was attributed to the large exchange anisotropy which exists due to the quasi-2D structure of the layered (NH(3)OH)(2)CoF(4) material.
Subject(s)
Chemistry, Physical/methods , Cobalt/chemistry , Fluorine Compounds/chemistry , Quaternary Ammonium Compounds/chemistry , Algorithms , Anisotropy , Hot Temperature , Magnetic Fields , Magnetics , Molecular Conformation , Phase Transition , Pressure , TemperatureABSTRACT
The hydrothermal treatment of an appropriate suspension of Ba and Fe hydroxides in the presence of a large excess of OH(-) results in the formation of Ba hexaferrite at temperatures as low as 150 degrees C. This low formation temperature enables the synthesis of uniform, ultrafine Ba hexaferrite nanoparticles. These nanoparticles have a disc-like shape, approximately 10 nm wide, but only approximately 3 nm thick. When the temperature of the hydrothermal treatment is increased, large platelet Ba hexaferrite crystals appear as a consequence of secondary re-crystallization (Ostwald ripening). In this work, this undesired process of secondary re-crystallization has been evaluated. We show that the secondary re-crystallization can be totally suppressed with the use of an oleic acid surfactant. The addition of oleic acid enabled the synthesis of uniform, ultrafine nanoparticles at temperatures up to 240 degrees C. The nanoparticles were hydrophobic and could be suspended in nonpolar liquids to form relatively concentrated ferrofluids. Such stable suspensions of hexaferrite nanoparticles will be technologically important, especially as precursors for the preparation of new nanostructured materials, for example nanocomposites or nanostructured ceramic films.
ABSTRACT
Stable suspensions of superparamagnetic iron oxide nanoparticles in water (water-based ferrofluids) were prepared using citric acid (CA) as a surfactant. The influences of different factors on the amount of nanoparticles in a stable suspension were systematically studied. These factors, including the temperature, the pH value and the concentration of CA applied during the adsorption of the CA onto the nanoparticles and during their suspension in water, were evaluated. The highest content of nanoparticles in a stable suspension was obtained when the CA was absorbed at pH values of around 5.2, where two carboxyl groups are dissociated, and when the nanoparticles were suspended at a pH of around 10, where all three carboxyl groups of the CA are in a dissociated state.
ABSTRACT
Nanoparticles of zinc-doped maghemite were prepared using ultrasonic radiation. As a precursor, a suspension of maghemite in an alkaline aqueous solution of zinc nitrate at pH 9 was sonicated. The zinc-doped maghemite nanoparticles were investigated by X-ray diffraction, Mössbauer spectroscopy, high-resolution electron microscopy (HREM) and SQUID magnetometry. The Mössbauer measurements, which cover the temperature range 4.2 K to room temperature, were acquired in zero field and an applied field of 5 T. The results show that by using ultrasound radiation, zinc Zn2+ can substitute for Fe3+ up to a composition close to zinc ferrite (ZnFe2O4), which has a random distribution of Fe3+ ions over both A and B sublattices in the spinel structure with an inversity parameter of delta=0.322. This leads to a maximum saturation magnetization (Ms) of 64.1 emu/g at 300 K and 73.5 emu/g at 2 K.
ABSTRACT
In a questionnaire with 295 out-patients with gynecological cancers 51% had undergone paramedical treatment. This medication was given additionally to traditional treatment. The effect of paramedical proceedings was supposed to be good in most of the patients.