Physical Ageing of Amorphous Poly(lactic acid)-Indapamide System Studied by Differential Scanning Calorimetry.

The process of isothermal and non-isothermal physical ageing of amorphous polylactide (PLA) with the active pharmaceutical ingredient, indapamide (IND), was investigated. A PLA-IND system with a 50/50 weight ratio was obtained and characterized using differential scanning calorimetry (DSC). In the 50/50 (w/w) mixture, two glass transitions were observed: the first at 64.1 ± 0.3 °C corresponding to the glass transition temperature (Tg) of PLA, and the second at 102.6 ± 1.1 °C corresponding to the Tg of IND, indicating a lack of molecular mixing between the two ingredients. The PLA-IND system was subjected to the isothermal physical ageing process at different ageing temperatures (Ta) for 2 h. It was observed that the highest effect of physical ageing (enthalpy relaxation change) on IND in the PLA-IND system occurred at Ta = 85 °C. Furthermore, the system was annealed for various ageing times at 85 °C. The relaxation enthalpies were estimated for each experiment and fitted to the Kohlrausch-Williams-Watts (KWW) equation. The KWW equation allowed for the estimation of the relaxation time and the parameter describing the distribution of relaxation times of the isothermal physical ageing process of IND in the PLA-IND system. The physical ageing of the PLA-IND mixture (50/50) was also discussed in the context of heat capacity. Moreover, the activation energy and fragility parameters were determined for the PLA-IND (50/50) system.

Physical Ageing of Amorphous Indapamide Characterised by Differential Scanning Calorimetry.

The objective of this study was to characterise amorphous indapamide (IND) subjected to the physical ageing process by differential scanning calorimetry (DSC). The amorphous indapamide was annealed at different temperatures below the glass transition, i.e., 35, 40, 45, 65, 75 and 85 °C for different lengths of time, from 30 min up to a maximum of 32 h. DSC was used to characterise both the crystalline and the freshly prepared glass and to monitor the extent of relaxation at temperatures below the glass transition (Tg). No ageing occurred at 35, 40 and 45 °C at the measured lengths of times. Molecular relaxation time constants (τKWW) for samples aged at 65, 75 and 85 °C were determined by the Kohlrausch-Williams-Watts (KWW) equation. The fragility parameter m (a measure of the stability below the glass transition) was determined from the Tg dependence from the cooling and heating rates, and IND was found to be relatively stable ("moderately fragile") in the amorphous state. Temperature-modulated DSC was used to separate reversing and nonreversing processes for unaged amorphous IND. The enthalpy relaxation peak was clearly observed as a part of the nonreversing signal. Heat capacities data for unaged and physically aged IND were fitted to Cp baselines of solid and liquid states of IND, were integrated and enthalpy was presented as a function of temperature.