ABSTRACT
We investigate the hysteresis obtained in the hydrogen absorption and desorption cycle for a single crystal [Formula: see text] superlattice. Below the critical temperature, a small but clear hysteresis is observed in the pressure-composition isotherms, while it is absent above. The experimental results thereby prove the relevance of macroscopic energy barriers for obtaining hysteresis in coherent structural transformations. The textured Pd layer exhibits substantially larger hysteresis effects, which can be related to an irreversible energy loss caused by defect generation in Pd.
ABSTRACT
The chemical diffusion coefficient of hydrogen in a 50 nm thin film of vanadium (0 0 1) is measured as a function of concentration and temperature, well above the known phase boundaries. Arrhenius analysis of the tracer diffusion constants reveal large changes in the activation energy with concentration: from 0.10 at 0.05 in H V-1 to 0.5 eV at 0.2 in H V-1. The results are consistent with a change from tetrahedral to octahedral site occupancy, in that concentration range. The change in site occupancy is argued to be caused by the uniaxial expansion of the film originating from the combined hydrogen induced expansion and the clamping of the film to the substrate.