Covalent bonding of N-hydroxyphthalimide on mesoporous silica for catalytic aerobic oxidation of p-xylene at atmospheric pressure.

The surface of SBA-15 mesoporous silica was modified by N-hydroxyphthalimide (NHPI) moieties acting as immobilized active species for aerobic oxidation of alkylaromatic hydrocarbons. The incorporation was carried out by four original approaches: the grafting-from and grafting-onto techniques, using the presence of surface silanols enabling the formation of particularly stable O-Si-C bonds between the silica support and the organic modifier. The strategies involving the Heck coupling led to the formation of NHPI groups separated from the SiO2 surface by a vinyl linker, while one of the developed modification paths based on the grafting of an appropriate organosilane coupling agent resulted in the active phase devoid of this structural element. The successful course of the synthesis was verified by FTIR and 1H NMR measurements. Furthermore, the formed materials were examined in terms of their chemical composition (elemental analysis, thermal analysis), structure of surface groups (13C NMR, XPS), porosity (low-temperature N2 adsorption), and tested as catalysts in the aerobic oxidation of p-xylene at atmospheric pressure. The highest conversion and selectivity to p-toluic acid were achieved using the catalyst with enhanced availability of non-hydrolyzed NHPI groups in the pore system. The catalytic stability of the material was additionally confirmed in several subsequent reaction cycles.

Abiotic weathering of plastic: Experimental contributions towards understanding the formation of microplastics and other plastic related particulate pollutants.

The increasing use of plastic (synthetic polymers) results in the release of uncontrollable amounts of synthetic materials into the environment through waste, infrastructure, and essential goods. As plastic materials undergo weathering, a complex process unfolds, leading to the formation of pollutants, notably microplastics. This study employs multiple instrumental methods to explore the intricate abiotic degradation of the five most commonly used synthetic polymers in environmentally relevant conditions. An extensive set of analytical techniques, along with chemometric analysis of the results of Raman spectroscopy, was used to characterize the materials and evaluate the nature and extent of degradation caused by artificial weathering under temperature, humidity, and solar-like irradiation cycles. Investigation focuses on the link between abiotic weathering and the generation of micro- and nanoplastics, accompanied by molecular and surface adhesion changes, and the release of additives such as metals and metal oxides. Research reveals that microplastics may exhibit varied physical properties due to the incorporation of significant quantities of high-density additives from the parent plastic, which might influence the extraction methods and the transportation models' accuracy. At the molecular and microscopic scales, non-homogeneous pathways through which plastic decomposes during weathering were observed. The formation of additive-polymer combinations might play a pivotal role in the monitoring approaches for microplastics, presenting unique challenges in assessing the environmental impact of different plastic types. These findings offer complex insight into abiotic weathering, microplastics' generation, and the influence of additives that were previously overlooked in toxicity and health assessment studies. As plastic pollution continues to escalate, understanding these complex processes is crucial for microplastic monitoring development and adopting effective preventative measures.

In Search of Factors Determining Activity of Co3O4 Nanoparticles Dispersed in Partially Exfoliated Montmorillonite Structure.

The paper discusses a formation of Mt-PAA composite containing a natural montmorillonite structure partially exfoliated by poly(acrylic acid) introduced through intercalation polymerization of acrylic acid. Mt-PAA was subsequently modified by controlled adsorption of Co2+ ions. The presence of aluminosilicate packets (clay) and carboxyl groups (hydrogel) led to the deposition of significant amounts of Co2+ ions, which after calcination formed the Co3O4 spinel particles. The conditions of the Co2+ ions' deposition (pH, volume and concentration of Co(NO3)2 solution, as well as a type of pH-controlling agent) were widely varied. Physicochemical characterization of the prepared materials (including X-ray fluorescence (XRF), X-ray powder diffraction (XRD), low-temperature nitrogen adsorption, X-ray photoelectron spectroscopy (XPS) and temperature-programmed reduction (H2-TPR)) revealed that the modification conditions strongly influenced the content as well as the distribution of the Co3O4 active phase, tuning its reducibility. The latter parameter was, in turn, very important from the point of view of catalytic activity in the combustion of aromatic volatile organic compounds (VOCs) following the Mars-van Krevelen mechanism.

Investigation on the low-temperature transformations of poly(furfuryl alcohol) deposited on MCM-41.

MCM-41-type mesoporous silica was used as a support for poly(furfuryl alcohol) deposition. This material was produced by precipitation-polycondensation of furfuryl alcohol (FA) in aqueous slurry of the SiO2 support followed by controlled partial carbonization. By tuning the FA/MCM-41 mass ratio in the reaction mixture, various amounts of polymer particles were introduced on the inner and outer surface of the MCM support. The thermal decomposition of the PFA/MCM-41 composites was studied by thermogravimetry (TG) and spectroscopic techniques (DRIFT, XPS), whereas the evolution of textural parameters with increasing polymer content was investigated using low-temperature adsorption of nitrogen. The mechanism of thermal transformations of PFA deposited on the MCM-41 surface was discussed in detail. It was found that heating at a temperature of about 523 K resulted in opening of the furan rings and the formation of γ-diketone moieties, which were found to be the highest effective surface species for the adsorption of polar volatile organic compounds. A further increase in calcination temperature caused a drop in the amounts of surface carbonyls and the appearance of condensed aromatic domains.