ABSTRACT
This study examined the effects of liquid nitrogen vapor on osteogenesis in the rabbit femur. Cryotweezers made of porous nickel titanium alloy (nitinol or NiTi) obtained by self-propagating high temperature synthesis were used in this experiment. The porous structure of the cryotweezers allows them to hold up to 10 g of liquid nitrogen after being immersed for 2 min, which completely evaporates after 160 s. To study the effects of liquid nitrogen evaporation on osteogenesis, a rabbit femur was perforated. The formed holes were subjected to cryotherapy with varying exposure times. It was found that a 3 s exposure time stimulates osteogenesis, which was manifested in a greater number of osteoblasts in the regenerate compared to the control sample without liquid nitrogen. It was observed that increasing the exposure to 6, 9 or 12 s had a destructive effect, to varying degrees. The most severe damage was exerted by a 12 s exposure, which resulted in the formation of osteonecrosis areas. In the samples exposed to 6 and 9 s of cryotherapy, destruction of the cytoplasm of osteocytes and osteoclasts was observed.
Subject(s)
Alloys , Cryotherapy , Femur , Nickel , Osteogenesis , Titanium , Animals , Rabbits , Cryotherapy/methods , Nickel/chemistry , Porosity , Femur/drug effects , Titanium/chemistry , Alloys/chemistry , Osteogenesis/drug effects , Nitrogen , Osteoblasts/drug effects , Osteoblasts/cytology , Osteonecrosis/therapy , Male , Osteoclasts/drug effects , Osteocytes/drug effects , Osteocytes/cytologyABSTRACT
Coatings based on calcium phosphate with thicknesses of 0.5 and 2 µm were obtained by high-frequency magnetron sputtering on NiTi substrates in an argon atmosphere. The coating was characterized using X-ray diffraction, scanning electron microscopy, atomic force microscopy, and in vitro cytocompatibility and bioactivity studies. A biphasic coating of tricalcium phosphate (Ca3(PO4)2) and hydroxyapatite (Ca10(PO4)6(OH)2) with a 100% degree of crystallinity was formed on the surface. The layer enriched in calcium, phosphorus, and oxygen was observed using scanning electron microscopy and energy-dispersive X-ray spectroscopy. Scanning electron microscopy showed that the surface structure is homogeneous without visible defects. The 2 µm thick coating obtained by sputtering with a deposition time of 4 h and a deposition rate of 0.43 µm/h is uniform, contains the highest amount of the calcium phosphate phase, and is most suitable for the faster growth of cells and accelerated formation of apatite layers. Samples with calcium phosphate coatings do not cause hemolysis and have a low cytotoxicity index. The results of immersion in a solution simulating body fluid show that NiTi with the biphasic coating promotes apatite growth, which is beneficial for biological activity.