ABSTRACT
We investigate 1D nanostructures based on a Mo6@SU8 hybrid nanocomposite in which photoluminescent Mo6 clusters are embedded in the photosensitive SU8 resist. Tens of micrometers long Mo6@SU8-based tubular nanostructures were fabricated by the wetting template method, enabling the control of the inner and outer diameter to about 190 nm and 240 nm respectively, as supported by structural and optical characterizations. The image plane optical study of these nanotubes under optical pumping highlights the efficient waveguiding phenomenon of the red luminescence emitted by the clusters. Moreover, the wave vector distribution in the Fourier plane determined by leakage radiation microscopy gives additional features of the emission and waveguiding. First, the anisotropic red luminescence of the whole system can be attributed to the guided mode along the nanotube. Then, a low-loss propagation behavior is evidenced in the Mo6@SU8-based nanotubes. This result contrasts with the weaker waveguiding signature in the case of UV210-based nanotubes embedding PFO (poly(9,9-di-n-octylfluorenyl-2,7-diyl)). It is attributed to the strong reabsorption phenomenon, owing to overlapping between absorption and emission bands in the semi-conducting conjugated polymer PFO. These results make this Mo6@SU8 original class of nanocomposite a promising candidate as nanosources for submicronic photonic integration.
ABSTRACT
The combined time-resolved photoluminescence (PL) and theoretical study performed on luminescent [Mo6Br(i)8Br(a)6](2-)-based systems unambiguously shows that their NIR-luminescence is due to at least two emissive states. By quantum chemical studies, we show for the first time that important geometrical relaxations occur at the triplet states either by the outstretching of an apex away from the square plane of the Mo6 octahedron or by the elongation of one Mo-Mo bond. Experimental PL measurements demonstrate that the external environment (counter-ions, crystal packing) of the cluster has a noticeable impact on its relaxation processes. Temperature and excitation wavelength dependence of the two components of the luminescence spectra is representative of multiple competitive de-excitation processes in contradiction with Kasha's rule. Our results also demonstrate that the relaxation processes before and after emission can be tracked via fast time-resolved spectroscopy. They also show that the surroundings of the luminescent cluster unit and the excitation wavelength could be modulated for target applications.
ABSTRACT
The radial nanostructure of the binary liquid triethylamine/water confined in 60 nm diameter independent cylindrical pores of anodic aluminium oxide membranes is studied by small angle neutron scattering. It is shown that composition inhomogeneities are present in the confined mixtures well below the bulk critical point. An analysis of the neutron scattering form factor reveals the existence of an adsorbed water layer of a few nanometers at the liquid/alumina interface, coexisting with a TEA-rich phase in the core.