ABSTRACT
Glass of the composition 70%B2 O3 -(30-x)%Na2 O-x%Y2 O3 with x = 0, 0.5, 1, 1.5, 2, and 2.5 mol% was manufactured using the melt quenching method. X-ray diffraction tests indicated the amorphous structure of the glass, with the presence of some YBO3 clusters in the high yttrium content samples. Fourier transform infrared spectra analysis proved the presence of different borate groups and linkages, in addition to nonsystematic changes in the ratio BO3 /BO4 in the glass. The forming ability of the glass was found to be approximately stable for the low Y3+ content samples and increased for the heavily doped samples. The density of the samples was found to increase as the Y3+ concentration was increased, whereas the molar volume decreased. The bond strength of the examined glass suggested that a covalent nature was dominant between bonds. All the Y3+ -doped glass was found to emit greenish-cyan light when excited at λ ex = 365 nm . Photoluminescence intensity was shown to be enhanced by the generated YBO3 groups. The obtained correlated colour temperature values with 82.5% purity recommend the suitability of the glass for applications in outdoor illumination.