Electrospinning of collagen and elastin for tissue engineering applications.

Meshes of collagen and/or elastin were successfully prepared by means of electrospinning from aqueous solutions. Flow rate, applied electric field, collecting distance and composition of the starting solutions determined the morphology of the obtained fibres. Addition of PEO (M(w)=8 x 10(6)) and NaCl was always necessary to spin continuous and homogeneous fibres. Spinning a mixture of collagen and elastin resulted in fibres in which the single components could not be distinguished by SEM. Increasing the elastin content determined an increase in fibres diameters from 220 to 600 nm. The voltage necessary for a continuous production of fibres was dependent on the composition of the starting solution, but always between 10 and 25 kV. Under these conditions, non-woven meshes could be formed and a partial orientation of the fibres constituting the mesh was obtained by using a rotating tubular mandrel as collector. Collagen/elastin (1:1) meshes were stabilized by crosslinking with N-(3-dimethylaminopropyl)-N'-ethylcarbodiimide hydrochloride (EDC) and N-hydroxysuccinimide (NHS). This treatment afforded materials with a high thermal stability (T(d)=79 degrees C) without altering their original morphology. Upon crosslinking PEO and NaCl were fully leached out. Smooth muscle cells grew as a confluent layer on top of the crosslinked meshes after 14 d of culture.

First steps towards tissue engineering of small-diameter blood vessels: preparation of flat scaffolds of collagen and elastin by means of freeze drying.

Porous scaffolds composed of collagen or collagen and elastin were prepared by freeze drying at temperatures between -18 and -196 degrees C. All scaffolds had a porosity of 90-98% and a homogeneous distribution of pores. Freeze drying at -18 degrees C afforded collagen and collagen/elastin matrices with average pore sizes of 340 and 130 mum, respectively. After 20 successive cycles up to 10% of strain, collagen/elastin dense films had a total degree of strain recovery of 70% +/- 5%, which was higher than that of collagen films (42% +/- 6%). Crosslinking of collagen/elastin matrices either in water or ethanol/water (40% v/v) was carried out using a carbodiimide (N-(3-dimethylaminopropyl)-N'-ethylcarbodiimide hydrochloride, EDC) in combination with a succinimide (N-hydroxysuccinimide, NHS) in the presence or absence of a diamine (J230) or by reaction with butanediol diglycidylether (BDGE), followed by EDC/NHS. Crosslinking with EDC/NHS or EDC/NHS/J230 resulted in matrices with increased stiffness as compared to noncrosslinked matrices, whereas sequential crosslinking with the diglycidylether and EDC/NHS yielded very brittle scaffolds. Ethanol/water was the preferred solvent in the crosslinking process because of its ability to preserve the open porous structure during crosslinking. Smooth muscle cells were seeded on the (crosslinked) scaffolds and could be expanded during 14 days of culturing.

A novel time resolved fluorometric assay of anoikis using Europium-labelled Annexin V in cultured adherent cells.

BACKGROUND: Adherent cells undergo apoptosis when detached from their home ground, a process called anoikis (homelessness). METHODS: We developed a new and sensitive method to analyse apoptosis and anoikis of adherent cell types using a time resolved fluorometric assay with Europium-labelled Annexin V. Anoikis was induced with tumor necrosis factor-alpha/cycloheximide and three cell fractions of the cell cultures were prepared and analysed. Fraction 1 consisted of adherent cells, analysed while growing on their support (without detachment by trypsinisation). Fraction 2 contained detached cells due to anoikis (floating cells) and fraction 3 contained apoptotic bodies. Both fractions 2 and 3 were present in the culture medium and were isolated by differential centrifugation. RESULTS: TNF-alpha treatment of three different types of adherent cell cultures induced a significant increase of the amount of floating cells (anoikis) and apoptotic bodies compared to control cell cultures. Also in the adherent cell fractions a small amount of apoptosis was observed. CONCLUSIONS: The novel time resolved assay provides the ability to analyse the cell death cascade in adherent cell cultures of the same sample at the same time in a sensitive and reproducible way.

Analysis of the balance between proliferation and apoptosis of cultured vascular smooth muscle cells for tissue-engineering applications.

Tissue homeostasis, the balance between cell proliferation and apoptosis, is an important factor in tissue engineering. We describe a new method to analyze markers of both proliferation and apoptosis in a single assay to monitor growth behavior of cell cultures. Human vascular smooth muscle cells (VSMCs) were cultured either on gelatin-coated tissue culture polystyrene or in three-dimensional porous scaffolds composed of insoluble collagen and elastin. mRNA concentrations of cyclin E, as a marker of proliferation, and of tissue transglutaminase (tTG) as a marker of apoptosis, quantified by a real-time reverse transcriptase-polymerase chain reaction (RT-PCR) and normalized to porphobilinogen deaminase mRNA concentrations, were analyzed. tTG mRNA expression levels were increased when apoptosis was induced by tumor necrosis factor-alpha in combination with cycloheximide or by culturing the cells in serum-free culture medium. Cyclin E mRNA expression levels were less altered in these cell cultures. Results were compared with several reference tests to measure apoptosis including DNA fragmentation, annexin V staining, and light microscopy. This RT-PCR method could be used to characterize cell growth behavior of VSMCs in vitro. In addition, it was shown that this test is suitable to measure the balance between proliferation and apoptosis of VSMCs present in tissue-engineered constructs.