ABSTRACT
A current drawback of spintronics is the large power that is usually required for magnetic writing, in contrast with nanoelectronics, which relies on "zero-current," gate-controlled operations. Efforts have been made to control the spin-relaxation rate, the Curie temperature, or the magnetic anisotropy with a gate voltage, but these effects are usually small and volatile. We used ferroelectric tunnel junctions with ferromagnetic electrodes to demonstrate local, large, and nonvolatile control of carrier spin polarization by electrically switching ferroelectric polarization. Our results represent a giant type of interfacial magnetoelectric coupling and suggest a low-power approach for spin-based information control.
ABSTRACT
Ferroelectrics possess a polarization that is spontaneous, stable and electrically switchable, and submicrometre-thick ferroelectric films are currently used as non-volatile memory elements with destructive capacitive readout. Memories based on tunnel junctions with ultrathin ferroelectric barriers would enable non-destructive resistive readout. However, the achievement of room-temperature polarization stability and switching at very low thickness is challenging. Here we use piezoresponse force microscopy at room temperature to show robust ferroelectricity down to 1 nm in highly strained BaTiO(3) films; we also use room-temperature conductive-tip atomic force microscopy to demonstrate resistive readout of the polarization state through its influence on the tunnel current. The resulting electroresistance effect scales exponentially with ferroelectric film thickness, reaching approximately 75,000% at 3 nm. Our approach exploits the otherwise undesirable leakage current-dominated by tunnelling at these very low thicknesses-to read the polarization state without destroying it. We demonstrate scalability down to 70 nm, corresponding to potential densities of >16 Gbit inch(-2). These results pave the way towards ferroelectric memories with simplified architectures, higher densities and faster operation, and should inspire further exploration of the interplay between quantum tunnelling and ferroelectricity at the nanoscale.