ABSTRACT
BACKGROUND: The objective was to investigate the radiopacity of 11 commercial posterior restorative materials by establishing their mean gray values (MGVs) and comparing them with dental hard tissues. METHODS AND MATERIALS: Five-disc specimens were prepared for each of the following materials: Cerasmart 270 CAD/CAM block A3LT (CS), Amalgam (A), Ketac Molar A3 (KM), Cention-N A2 (CN), G-aenial Universal Flo AO2 (GO2) and A2 (G2), Ever-X Flow Dentine (EXD) and Bulk (EXB) shades, Equia Forte HT Fil A2 (EF2) and A3 (EF3), and Equia Fil A3 (E3). Freshly extracted maxillary premolar teeth were used as a control. The MGVs of specimens and a 10-step aluminum stepwedge (Al) were measured with Adobe Photoshop. ANOVA and Dunnett T3 tests were used to assess the significance of the differences (α=0.05). RESULTS: Statistically significant differences were revealed between some of the groups. Amalgam had the highest radiopacity. The radiopacity of dentin and CS were close to that of 1 mm Al. G2, KM, GO2, EXB, and EXD showed higher mean radiopacity than dentin. Enamel had a radiopacity equivalent to 2 mm Al. CN, EF2, and E3 had higher mean radiopacity than enamel. CONCLUSIONS: All materials met the ISO requirements. Alkasite and reinforced glass ionomer restoratives demonstrated higher mean radiopacity than the posterior flowable composites. Material shades did not affect the radiopacity.
Subject(s)
Composite Resins , Dentin , Dentin/diagnostic imaging , Dental Materials , Dental Enamel , Materials TestingABSTRACT
OBJECTIVE: This study examined the effect of Er,Cr:YSGG laser irradiation on the microtensile bond strength (microTBS) of a three-step etch-and-rinse and a two-step self-etch adhesive to sound and caries-affected dentin. METHODS: Sixteen freshly extracted human molars with occlusal dentin caries were used. The caries lesion was removed by one of the following methods: conventional treatment with burs or Er,Cr:YSGG laser (Waterlase MD, Biolase). The adhesive systems (AdheSE, Ivoclar Vivadent and Scotchbond Multi Purpose, 3M ESPE) were applied to the entire tooth surface according to the manufacturers' instructions. Resin composites were applied to the adhesive-treated dentin surfaces and light-cured. Each tooth was sectioned into multiple beams with the "non-trimming" version of the microtensile test. The specimens were subjected to microtensile forces (BISCO Microtensile Tester, BISCO). The data was analyzed by three-way ANOVA and independent t-tests (p=0.05). RESULTS: Er,Cr:YSGG laser irradiation exhibited similar microTBS values compared to that of conventional bur treatment, regardless of the adhesive system and type of treated dentin. The self-etch system revealed lower microTBS values, both with conventional and laser treatment techniques, compared to the etch-and-rinse adhesive in sound and caries-affected dentin (p<0.05). CONCLUSION: Er,Cr:YSGG laser irradiation did not negatively affect the bonding performance of adhesive systems to sound and caries-affected dentin.
Subject(s)
Dental Bonding , Dental Cavity Preparation , Dental Stress Analysis , Dentin/radiation effects , Lasers, Solid-State , Adhesives , Composite Resins , Humans , In Vitro Techniques , Tensile StrengthABSTRACT
OBJECTIVES: This study: 1) analyzed the surface roughness of five novel resin composites that contain nanoparticles after polishing with three different one-step systems and 2) evaluated the effectiveness of these polishers and their possible surface damage using scanning electron microscope (SEM) analysis. METHODS: The resin composites evaluated in this study include CeramX, Filtek Supreme XT, Grandio, Premise and Tetric EvoCeram. A total of 100 discs (20/resin composites, 10 x 2 mm) were fabricated. Five specimens/resin composites cured under Mylar strips served as the control. The samples were polished for 30 seconds with PoGo, OptraPol and One Gloss discs at 15,000 rpm using a slow speed handpiece. The surfaces were tested for roughness (Ra) with a surface roughness tester and examined with SEM. One-way ANOVA was used for statistical analysis (p = 0.05). RESULTS: For all the composites tested, differences between the polishing systems were found to be significant (p < 0.05). For Filtek Supreme XT, Mylar and PoGo created equally smooth surfaces, while significantly rougher surfaces were obtained after OptraPol and One Gloss applications. For Grandio, Mylar and PoGo created equally smooth surfaces, while OptraPol and One Gloss produced equally rougher surfaces. Tetric EvoCeram exhibited the roughest surface with OptraPol, while no significant differences were found between Premise and CeramX. According to SEM images, OptraPol and One Gloss scratched and plucked the particles away from the surface, while PoGo created a uniform finish, although the roughness values were not the same for each composite. CONCLUSION: Effectiveness of the polishers seems to be material dependent.
Subject(s)
Composite Resins/chemistry , Dental Materials/chemistry , Dental Polishing/methods , Dental Polishing/instrumentation , Glass/chemistry , Humans , Humidity , Light , Materials Testing , Microscopy, Electron, Scanning , Nanoparticles/chemistry , Polyethylene Terephthalates/chemistry , Radiation Dosage , Surface Properties , TemperatureABSTRACT
Dentin bonding agents with antibacterial effects may inhibit secondary caries formation and pulp inflammation by eliminating residual bacteria in and on dentin. Therefore, the antibacterial effects of Prime & Bond NT (PB), Prime & Bond NT without fluoride (PBNF), Gluma Comfort Bond (GL), ABF, Xeno CF II (XE), 2-hydroxyethyl methacrylate (HEMA), triethylene glycol dimethacrylate (TEG-DMA), and 0.2% chlorhexidine were tested against Streptococcus mutans, S. sobrinus, and Lactobacillus acidophilus using the agar-diffusion method with and without bovine-dentin disks (200 microm and 500 microm thickness) placed between the bacteria and the test substances. Without dentin, ABF Primer showed growth inhibition for all bacterial strains. XE inhibited S. mutans and S. sobrinus, and PB S. sobrinus. ABF Bonding inhibited L. acidophilus. PBNF, HEMA, and TEGDMA did not have any antibacterial effects. Dentin disks of 500 microm thickness reduced the inhibitory effect of chlorhexidine to 23% to 54% compared with direct application. ABF Primer (nonpolymerized) produced inhibition zones against all tester strains regardless of dentin disks interposed or not. XE (against S. mutans and S. sobrinus) and PB (against S. sobrinus) did not produce any inhibition zones on 200 microm thick dentin. After polymerization, the ABF system did not inhibit bacterial growth on 200 microm thick dentin disks. A dentin barrier reduces significantly the antibacterial activity of chlorhexidine and dentin bonding agents.