ABSTRACT
Aqueous colloidal silver nanoparticles have substantial potential in biological application as markers and antibacterial agents and in surface-enhanced Raman spectroscopy applications. A simple method of fabrication and encapsulation into an inert shell is of great importance today to make their use ubiquitous. Here we show that colloids of silver-core/silica-shell nanoparticles can be easily fabricated by a laser-ablation-assisted chemical reduction method and their sizes can be tuned in the range of 2.5 to 6.3 nm by simply choosing a proper water-ethanol proportion. The produced silver nanoparticles possess a porous amorphous silica shell that increases the inertness and stability of colloids, which decreases their toxicity compared with those without silica. The presence of a thin 2 to 3 nm silica shell was proved by EDX mapping. The small sizes of nanoparticles achieved by this method were analyzed using optical techniques, and they show typical photoluminescence in the UV-vis range that shifts toward higher energies with decreasing size.
ABSTRACT
Graphene, in single layer or multi-layer forms, holds great promise for future electronics and high-temperature applications. Resistance to oxidation, an important property for high-temperature applications, has not yet been extensively investigated. Controlled thinning of multi-layer graphene (MLG), e.g., by plasma or laser processing is another challenge, since the existing methods produce non-uniform thinning or introduce undesirable defects in the basal plane. We report here that heating to extremely high temperatures (exceeding 2000 K) and controllable layer-by-layer burning (thinning) can be achieved by low-power laser processing of suspended high-quality MLG in air in "cold-wall" reactor configuration. In contrast, localized laser heating of supported samples results in non-uniform graphene burning at much higher rates. Fully atomistic molecular dynamics simulations were also performed to reveal details of oxidation mechanisms leading to uniform layer-by-layer graphene gasification. The extraordinary resistance of MLG to oxidation paves the way to novel high-temperature applications as continuum light source or scaffolding material.
ABSTRACT
The accuracy of thermal conductivity measurements by the micro-Raman technique for suspended multi-layer graphene flakes has been shown to depend critically on the quality of the thermal contacts between the flakes and the metal electrodes used as the heat sink. The quality of the contacts can be improved by nonlocal laser annealing at increased power. The improvement of the thermal contacts to initially rough metal electrodes is attributed to local melting of the metal surface under laser heating, and increased area of real metal-graphene contact. Improvement of the thermal contacts between multi-layer graphene and a silicon oxide surface was also observed, with more efficient heat transfer from graphene as compared with the graphene-metal case.