Synthesis of nano-magnetic MnFe2O4 to remove Cr(III) and Cr(VI) from aqueous solution: A comprehensive study.

The co-precipitation method was used to synthesize nano-magnetic adsorbent MnFe2O4 (nMFO), characterized through XRD, SEM, EDS, and BET techniques. The synthesized nMFO was used for hexavalent and trivalent chromium ions elimination from the aqueous phase. The optimum pH for the adsorption of Cr (VI) and Cr (III) was determined as 2 and 5, respectively. The chromium ions adsorption behavior was well interpreted through the pseudo-second order kinetics model. Furthermore, isotherm studies were conducted, and the obtained results indicated that Langmuir isotherm model could well justify the chromium ions adsorption process. Quick removal (less than 10 min) of both chromium ions and high removal efficiency were occurred using nMFO. The utmost adsorption capacity of trivalent and hexavalent chromium ions were determined as 39.6 and 34.84 mg g-1, respectively. Thermodynamic studies on chromium adsorption revealed positive value for ΔH and negative value for ΔG, representing that chromium ions adsorption was an endothermic and spontaneous process. The multilinearity in the graphs of chromium ions adsorption was observed using intra-particle diffusion model. In this regard, the external mass transfer of chromium ions on synthesized nanoparticles was the important and controlling step in the adsorption process.

Immobilization of hexavalent chromium in contaminated soil using nano-magnetic MnFe2O4.

Nano-magnetic MnFe2O4 was prepared and examined to immobilize Cr(VI) in the soil. According to the results of scanning electron microscopy (SEM) and X-ray diffraction (XRD) the formation of nano-magnetic MnFe2O4 with the particle size of less than 200 nm was demonstrated. Compared with the untreated soil, the leachability of Cr(VI) was reduced from 70.95% to 4.22% through toxicity characteristic leaching procedure (TCLP) at a dosage of 2 g/L of nanoparticles and 192 h remediation time. At the same condition, the physiologically based extraction test (PBET) human bioaccessibility of chromium was reduced from 86.76% to 4.42%. Moreover, the plant bioavailability of hexavalent chromium (using EDTA) was reduced from 83.72% to 5.53%. According to the sequential extraction procedure (SEP) the loosely bounds Cr (90.28%) was converted to the relatively strong bound (Fe-Mn oxides fraction, 92.09%) revealed the significant decrease in risk of release and availability of chromium after immobilization procedure. Further, results of column experiments of Cr(VI) elution revealed that almost all of the water-soluble chromium was converted to the associated synthesized nanoparticles phase. Overall, the present study proved that nano-magnetic MnFe2O4 significantly enhanced the hexavalent chromium immobilization through a decrease in leachability, plant bioavailability, human bioaccessibility, and risk of release.