ABSTRACT
A combined experimental and computational approach is used to investigate the chemical transformations of kaolinite and metakaolin surfaces when exposed to sulfuric acid. These clay minerals are hydrated ternary metal oxides and are shown to be susceptible to degradation by loss of Al as the water-soluble salt Al2(SO4)3, due to interactions between H2SO4 and aluminum cations. This degradation process results in a silica-rich interfacial layer on the surfaces of the aluminosilicates, most prominently observed in metakaolin exposed to pH environments of less than 4. Our observations are supported by XPS, ATR-FTIR, and XRD experiments. Concurrently, DFT methodologies are used to probe the interactions between the clay mineral surfaces and H2SO4 as well as other sulfur-containing adsorbates. An analysis performed using a DFT + thermodynamics model shows that the surface transformation processes that lead to the loss of Al and SO4 from metakaolin are favorable at pH below 4; however, such transformations are not favorable for kaolinite, a result that agrees with our experimental efforts. The data obtained from both experimental techniques and computational studies support that the dehydrated surface of metakaolin interacts more strongly with sulfuric acid and provide atomistic insight into the acid-induced transformations of these mineral surfaces.
ABSTRACT
Toughness describes the ability of a material to resist fracture or crack propagation. It is demonstrated here that fracture toughness of a material can be asymmetric, i.e., the resistance of a medium to a crack propagating from right to left can be significantly different from that to a crack propagating from left to right. Such asymmetry is unknown in natural materials, but we show that it can be built into artificial materials through the proper control of microstructure. This paves the way for control of crack paths and direction, where fracture-when unavoidable-can be guided through predesigned paths to minimize loss of critical components.