ABSTRACT
Drinking water defluoridation has attracted significant attention in the scientific community, from which membrane technology, by exploring thin film nanocomposite (TFN) membranes, has demonstrated a great potential for treating fluoride-contaminated water. This study investigates the development of a TFN membrane by integrating titanium oxide nanosheets (TiO2 NSs) into the polyamide (PA) layer using interfacial polymerization. The characterization results suggest that successfully incorporating TiO2 NSs into the PA layer of the TFN membrane led to a surface with a high negative charge, hydrophilic properties, and a smooth surface at the nanoscale. The TFN membrane, containing 80 ppm of TiO2 NSs, demonstrated a notably high fluoride rejection rate of 98%. The Donnan-steric-pore-model-dielectric-exclusion model was employed to analyze the effect of embedding TiO2 NSs into the PA layer of TFN on membrane properties, including charge density (Xd), the pore radius (rp), and pore dielectric constant (εp). The results indicated that embedding TiO2 NSs increased Xd and decreased the εp by less than the TFC membrane without significantly affecting the rp. The resulting TFN membrane demonstrates promising potential for application in water treatment systems, providing an effective and sustainable solution for fluoride remediation in drinking water.
ABSTRACT
This study validates, for the first time, the effectiveness of two nanoclays, that is, cloisite (CS)-15A and montmorillonite (MNT) at the polyamide (PA) active layer in the reverse osmosis (RO) membrane. Cloisite-15A is natural montmorillonite modified with dimethyl dihydrogenated tallow quaternary ammonium salt. Thin-film composite (TFC) membranes were fabricated by the interfacial polymerization (IP) process between the trimesoylchloride (TMC)-n-hexane solution and m-phenylenediamine (MPD)-aqueous solution; the IP process took place on a polysulfone support sheet. The two types of nanoparticles were added in various weight ratios (0.005 wt.%-0.04 wt.%) in the n-hexane solution of TMC. Different characterizations like X-ray diffraction (XRD), contact angle, transmission electron microscopy (TEM), and membrane performance tests were performed to analyse the membrane properties. Both XRD and TEM studies proved that the two nanoclays are successfully anchored at the different sites of the PA layer. CS-15A could accelerate the water flux from 15 to 18.65 L/m2·h with NaCl rejection enhancement from 72% to 80%, relative to the control membrane. Conversely, MNT also enhanced the flux from 15 to 40 L/m2·h, but NaCl rejection reduced from 70% to 23%. The mechanism of water uptake in nanoclays was also discussed. The results pave the way for a complete future study, in which these phenomena should be studied in great detail.