Carbon-coated Fe-Mn-O composites as promising anode materials for lithium-ion batteries.

Fe-Mn-O composite oxides with various Fe/Mn molar ratios were prepared by a simple coprecipitation method followed by calcining at 600 °C, and carbon-coated oxides were obtained by pyrolyzing pyrrole at 550 °C. The cycling and rate performance of the oxides as anode materials are greatly associated with the Fe/Mn molar ratio. The carbon-coated oxides with a molar ratio of 2:1 exhibit a stable reversible capacity of 651.8 mA h g(-1) at a current density of 100 mA g(-1) after 90 cycles, and the capacities of 567.7, 501.3, 390.7, and 203.8 mA h g(-1) at varied densities of 200, 400, 800, and 1600 mA g(-1), respectively. The electrochemical performance is superior to that of single Fe3O4 or MnO prepared under the same conditions. The enhanced performance could be ascribed to the smaller particle size of Fe-Mn-O than the individuals, the mutual segregation of heterogeneous oxides of Fe3O4 and MnO during delithiation, and heterogeneous elements of Fe and Mn during lithiation.

Enhanced electrochemical performance of FeWO4 by coating nitrogen-doped carbon.

FeWO4 (FWO) nanocrystals were prepared at 180 °C by a simple hydrothermal method, and carbon-coated FWO (FWO/C) was obtained at 550 °C using pyrrole as a carbon source. The FWO/C obtained from the product hydrothermally treated for 5 h exhibits reversible capacities of 771.6, 743.8, 670.6, 532.6, 342.2, and 184.0 mAh g(-1) at the current densities of 100, 200, 400, 800, 1600, and 3200 mA g(-1), respectively, whereas that from the product treated for 0.5 h achieves a reversible capacity of 205.9 mAh g(-1) after cycling 200 times at a current density of 800 mA g(-1). The excellent electrochemical performance of the FWO/C results from the combination of the nanocrystals with good electron transport performance and the nitrogen-doped carbon coating.

Random composites of nickel networks supported by porous alumina toward double negative materials.

Random composites with nickel networks hosted randomly in porous alumina are proposed to realize double negative materials. The random composite for DNMs (RC-DNMs) can be prepared by typical processing of material, which makes it possible to explore new DNMs and potential applications, and to feasibly tune their electromagnetic parameters by controlling their composition and microstructure. Hopefully, various new RC-DNMs with improved performance will be proposed in the future.