Effect of hydrothermal pH values on the morphology of special microspheres of lignin-based porous carbon and the mechanism of carbon dioxide adsorption.

The study reports the economic and sustainable syntheses of a lignin-based porous carbon (LPC) for CO2 capture application. The pH values of hydrothermal solution affected the polymerization and aromatization of spheroidization, with morphological changes from blocky to microsphere. In addition, the reliable mechanisms of CO2 adsorption were proposed by combining experiments with Gaussian16 simulations based on DFT. The electrostatic attraction of oxygen-containing functional groups and the diffusivity resistance of CO2 in the pores are the key factors for the CO2 adsorption. ​The carboxyl groups have the strongest electrostatic attraction to CO2. LPC-pH 1 has the highest carboxyl group content, possessing a CO2 adsorption capacity of up to 5.10 mmol/g at 0℃, 1 bar. Furthermore, CO2 diffusion resistance became a main factor as the adsorption temperature increases. The innovative combination of quantum chemical calculations and microscopic properties provides a viable pathway for an insight into the future control of lignin-based carbon formation.

Biomass-based controllable morphology of carbon microspheres with multi-layer hollow structure for superior performance in supercapacitors.

The electrochemical properties of corn starch (CS)-based hydrothermal carbon microsphere (CMS) electrode materials for supercapacitor are closely related to their structures. Herein, cetyltrimethyl ammonium bromide (CTAB) was used as a soft template to form the corn starch (CS)-based carbon microspheres with radial hollow structure in the inner and middle layers by hydrothermal and sol-gel method. Due to the introduction of multi-layer hollow structure of carbon microsphere, more micropores were produced during CO2 activation, which increased the specific surface area and improved the capacitance performance. Compared to commercial activated carbon, the four different morphologies of corn starch CMS had better electrochemical performances. Consequently, the proposed CO2-(CTAB)-CS-CS exhibits a high discharge specific capacitance of 242.5F/g at 1 A/g in three-electrode system with 6 M KOH electrolyte, better than commercial activated carbon with 208.5F/g. Moreover, excellent stability is achieved for CO2-(CTAB)-CS-CS with approximately 97.14 % retention of the initial specific capacitance value after 10,000 cycles at a current density of 2 A/g, while the commercial activated carbon has 86.96 % retention. This implies that the corn starch-based multilayer hollow CMS could be a promising electrode material for high-performance supercapacitors.