ABSTRACT
The aim of this study was to determine the mechanical implications of four-unit fixed dental prostheses (FDPs) made of (1) monolithic zirconium dioxide (ZR O2), (2) polymethylmethacrylate (PMMA), (3) metal ceramic (PFM) and (4) impression resin (3DPP). METHODS: Four groups were studied with eight samples for each material (n: 32). Each structure was weighed, subjected to compressive tests and analyzed using 3D FEA. RESULTS: PMMA presented the lowest structural weight (1.33 g), followed by 3DPP (1.98 g), ZR O2 (6.34 g) and PFM (6.44 g). In fracture tests, PMMA presented a compressive strength of 2104.73 N and a tension of 351.752 MPa; followed by PFM, with a strength of 1361.48 N and a tension of 227.521 MPa; ZR O2, with a strength of 1107.63 N and a tension of 185.098 MPa; and 3DPP, with a strength of 1000.88 N and a tension of 143.916 MPa. According to 3D FEA, 3DPP presented the lowest degree of deformation (0.001 mm), followed by PFM (0.011 mm), ZR O2 (0.168 mm) and PMMA (1.035 mm). CONCLUSIONS: The weights of the materials did not have a direct influence on the mean values obtained for strength, stress or strain. Since the performance was related to the tension and forces supported by the structures in critical zones, the importance of considering design factors is clear. In vitro and 3D FEA assays allowed us to simulate different scenarios for the mechanical properties of certain materials before evaluating them clinically. Thus, they can generate predictions that would allow for the design of a better research methodology in future clinical trials.
ABSTRACT
In this article, an experimental investigation was conducted to study the effects of 3D printed structured fabrics on the tensile strength of two additive manufacturing technologies: (i) fused deposition modeling (FDM); and (ii) stereolithography (SLA). Three types of structured fabrics were designed in a linked fabric structure, which resembled the main characteristics of a conventional textile. Through computer-aided design (CAD), the textile structures were sketched, which, in a STL format, were transferred to 3D printing software, and consequently, they were printed. The specimens were subjected to tensile tests to analyse the behaviour of the linked structures under tensile loads. The results obtained indicated that the elements structured in a linked fabric pattern showed a statistically significant effect between the design of the 3D printed structured fabric and its tensile strength. Some important properties in textiles, fabric areal density, fineness (tex) and fabric flexibility were also analysed. This study opens an important field of research on the mechanical resistance of textile structures manufactured by 3D printing, oriented for applications in wearables that have a promising future in the fields of medicine, aerospace, sports, fashion, etc.