ABSTRACT
Multiwalled carbon nanotubes (MWCNTs) are interesting high-tech nanomaterials. MWCNTs oxidized and functionalized with itaconic acid and monomethylitaconate were demonstrated to be efficient additives for controlling nucleation of calcium carbonate (CaCO3) via gas diffusion (GD) in classical as well as nonclassical crystallization, yielding aragonite and truncated calcite. For the first time, all amorphous calcium carbonate (ACC) proto-structures, such as proto calcite-ACC, proto vaterite-ACC and proto aragonite-ACC, were synthesized via prenucleation cluster (PNC) intermediates and stabilized at room temperature. The MWCNTs also showed concentration-dependent nucleation promotion and inhibition similar to biomolecules in nature. Incorporation of fluorescein-5-thiosemicarbazide (5-FTSC) dye-labeled MWCNTs into the CaCO3 lattice resulted in fluorescent hybrid nanosized CaCO3. We demonstrate that functionalized MWCNTs offer a good alternative for controlled selective crystallization and for understanding an inorganic mineralization process.
ABSTRACT
Temperature and pH value can affect the short-range order of proto-structured and additive-free amorphous calcium carbonates (ACCs). Whereas a distinct change occurs in proto-vaterite (pv) ACC above 45 °C at pHâ 9.80, proto-calcite (pc) ACC (pHâ 8.75) is unaffected within the investigated range of temperatures (7-65 °C). IR and NMR spectroscopic studies together with EXAFS analysis showed that the temperature-induced change is related to the formation of proto-aragonite (pa) ACC. The data strongly suggest that the binding of water molecules induces dipole moments across the carbonate ions in pa-ACC as in aragonite, where the dipole moments are due to the symmetry of the crystal structure. Altogether, a (pseudo-)phase diagram of the CaCO3 polyamorphism in which water plays a key role can be formulated based on variables of state, such as the temperature, and solution parameters, such as the pH value.