Mode of Action of Zn-DOPOx and Melamine Polyphosphate as Flame Retardants in Glass Fiber-Reinforced Polyamide 66.

In this study, the flame retardant effect of the Zn salt of 10-hydroxy-9,10-dihydro-9-oxa-10-phosphaphenanthrene-10-oxide (Zn-DOPOx), melamine polyphosphate (MPP) and their mixture was investigated towards the mode of action in glass fiber-reinforced polyamide 66 (PA 66 GF). The flammability was evaluated using UL 94 V and cone calorimetry. Influence on char formation was analyzed by SEM. Thermal decomposition of Zn-DOPOx and MPP was studied by TGA and ATR-FTIR. The release of gaseous PA 66 decomposition products was investigated using TGA-DTA-FTIR. Combining Zn-DOPOx and MPP leads to an improvement in flame retardancy, most pronounced for equal parts of weight. Mode of action changes significantly for Zn-DOPOx:MPP (1:1) compared to the sole components and a strong interaction between Zn-DOPOx and MPP is revealed, resulting in a more open char structure. Fuel dilution as well as less exothermic decomposition are essential for the mode of action of the combination. Through low HRR values and high CO/CO2 ratio during cone calorimetry measurements, a significant increase in gas phase activity was proven. Therefore, it is concluded that Zn-DOPOx:MPP (1:1) leads to a significant increase in flame retardancy through a combination of mode of actions in the gas and condensed phase resulting from the change in thermal stability.

Structural and Magnetic Properties of BaFeO2.667 Synthesized by Oxidizing BaFeO2.5 Obtained via Nebulized Spray Pyrolysis.

A vacancy-ordered perovskite-type compound Ba3Fe3O8 (BaFeO2.667) was prepared by oxidizing BaFeO2.5 (P21/c) with the latter compound obtained by a spray pyrolysis technique. The structure of Ba3Fe3O8 was found to be isotypic to Ba3Fe3O7F (P21/m) and can be written as Ba3Fe3+2Fe4+1O8. Mössbauer spectroscopy and ab initio calculations were used to confirm mixed iron oxidation states, showing allocation of the tetravalent iron species on the tetrahedral site, and octahedral as well as square pyramidal coordination for the trivalent species within a G-type antiferromagnetic ordering. The uptake and release of oxygen were investigated over a broad temperature range from room temperature to 1100 °C under pure oxygen and ambient atmosphere via a combination of DTA/TG and variable temperature diffraction measurements. The compound exhibited a strong lattice enthalpy driven reduction to monoclinic and cubic BaFeO2.5 at elevated temperatures.

Metal-Support Interactions of Platinum Nanoparticles Decorated N-Doped Carbon Nanofibers for the Oxygen Reduction Reaction.

N-doped carbon materials are discussed as catalyst supports for the electrochemical oxygen reduction reaction (ORR) in fuel cells. This work deals with the preparation of Pt nanoparticles (NPs) supported on N-doped carbon nanofibers (N-CNF) from a polyaniline nanofiber (PANI NF) precursor, and investigates the ORR activity of the produced materials. Initially, Pt NPs are deposited on PANI NFs. The PANI NF precursors are characterized by near-edge X-ray absorption fine structure (NEXAFS) and transmission electron microscopy (TEM) measurements. It is shown, that in the PANI NF precursor materials electrons from the Pt are being transferred toward the π-conjugated systems of the aromatic ring. This strong interaction of Pt atoms with PANI explains the high dispersion of Pt NPs on the PANI NF. Subsequently, the PANI NF precursors are carbonized at different heat-treatment conditions resulting in structurally different N-CNFs which are characterized by NEXAFS, X-ray photoelectron spectroscopy (XPS) ,and TEM measurements. It is shown that an interaction between N-groups and Pt NPs exists in all investigated N-CNFs. However, the N-CNFs differ in the composition of the N-species and the dispersion of the Pt NPs. A small mean Pt NP size with a narrow size distribution is attributed to the presence of pyrdinic N-groups in the N-CNFs, whereas, for the N-CNFs with mainly graphitic and pyrrolic N-groups, an increase in the average Pt NP size with a broad size distribution is found. The ORR activity in alkaline media investigated by Koutecky-Levich analysis of rotating disk electrode measurements showed a largely enhanced ORR activity in comparison to a conventional Pt/C catalyst.

Surface-initiated anionic polymerization of [1]silaferrocenophanes for the preparation of colloidal preceramic materials.

A novel strategy for the preparation of poly(ferrocenylsilane) (PFS) immobilized on the surface of cross-linked polystyrene (PS) nanoparticles is reported. The ferrocene-containing core/shell architectures are shown to be excellent candidates as preceramic polymers yielding spherical ceramic materials consisting of iron silicide (Fe3 Si) and metallic iron after thermal treatment. For this purpose, dimethyl- and hydromethyl[1]silaferrocenophane monomers are polymerized by surface-initiated ring-opening polymerization upon taking advantage of residual vinylic moieties at the PS particle surface. A strategy for selective chain growth from the particle surface is developed without the formation of free PFS homopolymer in solution. The grafted particles are characterized using transmission electron microscopy (TEM) and dynamic light scattering (DLS). These particles are excellent precursors for ceramics as studied by thermogravimetric analysis (TGA). The composition of the ceramics is studied using X-ray diffraction (XRD) measurements, while the morphology is probed by scanning electron microscopy (SEM) revealing the original spherical shape of the precursor particles. Obtained ceramic materials- predominantly based on iron silicides-show ferromagnetic behavior as investigated by superconducting quantum interference device (SQUID) magnetization measurements at different temperatures.

Single-source-precursor synthesis of dense SiC/HfC(x)N(1-x)-based ultrahigh-temperature ceramic nanocomposites.

A novel single-source precursor was synthesized by the reaction of an allyl hydrido polycarbosilane (SMP10) and tetrakis(dimethylamido)hafnium(iv) (TDMAH) for the purpose of preparing dense monolithic SiC/HfC(x)N(1-x)-based ultrahigh temperature ceramic nanocomposites. The materials obtained at different stages of the synthesis process were characterized via Fourier transform infrared (FT-IR) as well as nuclear magnetic resonance (NMR) spectroscopy. The polymer-to-ceramic transformation was investigated by means of MAS NMR and FT-IR spectroscopy as well as thermogravimetric analysis (TGA) coupled with in situ mass spectrometry. Moreover, the microstructural evolution of the synthesized SiHfCN-based ceramics annealed at different temperatures ranging from 1300 °C to 1800 °C was characterized by elemental analysis, X-ray diffraction, Raman spectroscopy and transmission electron microscopy (TEM). Based on its high temperature behavior, the amorphous SiHfCN-based ceramic powder was used to prepare monolithic SiC/HfC(x)N(1-x)-based nanocomposites using the spark plasma sintering (SPS) technique. The results showed that dense monolithic SiC/HfC(x)N(1-x)-based nanocomposites with low open porosity (0.74 vol%) can be prepared successfully from single-source precursors. The average grain size of both HfC0.83N0.17 and SiC phases was found to be less than 100 nm after SPS processing owing to a unique microstructure: HfC0.83N0.17 grains were embedded homogeneously in a ß-SiC matrix and encapsulated by in situ formed carbon layers which acted as a diffusion barrier to suppress grain growth. The segregated Hf-carbonitride grains significantly influenced the electrical conductivity of the SPS processed monolithic samples. While Hf-free polymer-derived SiC showed an electrical conductivity of ca. 1.8 S cm(-1), the electrical conductivity of the Hf-containing material was analyzed to be ca. 136.2 S cm(-1).

Single-source-precursor synthesis of hafnium-containing ultrahigh-temperature ceramic nanocomposites (UHTC-NCs).

Amorphous SiHfBCN ceramics were prepared from a commercial polysilazane (HTT 1800, AZ-EM), which was modified upon reactions with Hf(NEt2)4 and BH3·SMe2, and subsequently cross-linked and pyrolyzed. The prepared materials were investigated with respect to their chemical and phase composition, by means of spectroscopy techniques (Fourier transform infrared (FTIR), Raman, magic-angle spinning nuclear magnetic resonance (MAS NMR)), as well as X-ray diffraction (XRD) and transmission electron microscopy (TEM). Annealing experiments of the SiHfBCN samples in an inert gas atmosphere (Ar, N2) at temperatures in the range of 1300-1700 °C showed the conversion of the amorphous materials into nanostructured UHTC-NCs. Depending on the annealing atmosphere, HfC/HfB2/SiC (annealing in argon) and HfN/Si3N4/SiBCN (annealing in nitrogen) nanocomposites were obtained. The results emphasize that the conversion of the single-phase SiHfBCN into UHTC-NCs is thermodynamically controlled, thus allowing for a knowledge-based preparative path toward nanostructured ultrahigh-temperature stable materials with adjusted compositions.

Visible light photocatalysis with c-WO(3-x)/WO3×H2O nanoheterostructures in situ formed in mesoporous polycarbosilane-siloxane polymer.

In recent years, there have been significant efforts to find novel photocatalytic materials with improved properties. Thus, there is an active ongoing search for new materials that can operate at a broad range of wavelengths for photocatalytic reactions. Among photocatalytically active semiconductors, considerable attention has been given to tungsten oxide with a band gap of E(g) ≈ 2.6 eV, which provides the opportunity to harvest visible light. In the present work, we report on a one-step synthesis of c-WO(3-x)/WO3×H2O nanowhiskers dispersed in a hydrolytically stable mesoporous polycarbosilane-siloxane ([-Si(O)CH2-]n) matrix. The as-synthesized nanocomposites possess high photocatalytic activity for the degradation of methylene blue (MB) under visible light irradiation. The enhanced photocatalytic activity is due to (i) the reduction in the electron-hole recombination rate because of the reduced dimensions of nanowhiskers, (ii) more efficient consumption of photogenerated electrons and holes as a result of the high surface-to-bulk-ratio of the nanowhiskers, and (iii) better electron-hole pair separation due to the formation of c-WO(3-x)/WO3×H2O nanoheterostructures.

Low temperature synthesis of nanocrystalline MnIn2O4 spinel.

Manganese indate, MnIn(2)O(4), with magnetic Mn(2+) ions on A-sites was synthesized by coprecipitation method followed by the calcination of the resulting precursor in air at 500 °C.

Effect of gas flow rates on the anatase-rutile transformation temperature of nanocrystalline TiO2 synthesised by chemical vapour synthesis.

Of the three crystallographic allotropes of nanocrystalline titania (rutile, anatase and brookite), anatase exhibits the greatest potential for a variety of applications, especially in the area of catalysis and sensors. However, with rutile being thermodynamically the most stable phase, anatase tends to transform into rutile on heating to temperatures in the range of 500 degrees C to 700 degrees C. Efforts made to stabilize the anatase phase at higher temperatures by doping with metal oxides suffer from the problems of having a large amorphous content on synthesis as well as the formation of secondary impurity phases on doping. Recent studies have suggested that the as-synthesised phase composition, crystallite size, initial surface area and processing conditions greatly influence the anatase to rutile transformation temperature. In this study nanocrystalline titania was synthesised in the anatase form bya chemical vapour synthesis (CVS) method using titanium tetra iso-propoxide (TTIP) as a precursor under varying flow rates of oxygen and helium. The anatase to rutile transformation was studied using high temperature X-ray diffraction (HTXRD) and simultaneous thermogravimetric analysis (STA), followed by transmission electron microscopy (TEM). It was demonstrated that the anatase-rutile transformation temperatures were dependent on the oxygen to helium flow rate ratio during CVS and the results are presented and discussed.

Crystallization behavior and controlling mechanism of iron-containing Si-C-N ceramics.

The crystallization behavior and controlling mechanism of the Si-Fe-C-N system based on polymer-derived SiCN ceramic filled with iron metal powder has been studied. The composite preparation conditions allow the formation of a random distribution of metallic particles in the polymer matrix volume for the Si-C-N system. Pyrolysis of the composite material at 1100 degrees C indicates the presence of one crystalline phase Fe(3)Si. While the sample pyrolyzed at 1200 degrees C reveals the formation of both Fe(3)Si and Fe(5)Si(3) phases, a crystallization of beta-SiC is additionally observed by increasing the temperature up to 1300 degrees C. The propensity for the formation of SiC is due to the presence of Fe(5)Si(3), where a solid-liquid-solid (SLS) growth mechanism was suggested to occur. X-ray diffraction (XRD), scanning electron microscopy (SEM), differential thermal analysis (DTA), and thermal gravimetric analysis with mass spectroscopic detection (TGA-MS) were employed to investigate the crystallization behavior of the Si-Fe-C-N system.

Defect structure in lithium-doped polymer-derived SiCN ceramics characterized by Raman and electron paramagnetic resonance spectroscopy.

Lithium-doped polymer-derived silicon carbonitride ceramics (SiCN:Li) synthesized at various pyrolysis temperatures, have been investigated by means of multifrequency and multipulse electron paramagnetic resonance (EPR) and Raman spectroscopy in order to determine different defect states that may impact the materials electronic properties. In particular, carbon- and silicon-based 'dangling bonds' at elevated, as well as metallic networks containing Li0 in the order of 1 microm at low pyrolysis temperatures have been observed in concentrations ranging between 10(14) and 10(17) spins mg(-1).