ABSTRACT
In this paper, we report a broad investigation of the optical properties of germanium (Ge) quantum-well devices. Our simulations show a significant increase of carrier density in the Ge quantum wells. Photoluminescence (PL) measurements show the enhanced direct-bandgap radiative recombination rates due to the carrier density increase in the Ge quantum wells. Electroluminescence (EL) measurements show the temperature-dependent properties of our Ge quantum-well devices, which are in good agreement with our theoretical models. We also demonstrate the PL measurements of Ge quantum-well microdisks using tapered-fiber collection method and quantify the optical loss of the Ge quantum-well structure from the measured PL spectra for the first time.
ABSTRACT
We demonstrate electroabsorption contrast greater than 5 dB over the entire telecommunication S- and C-bands with only 1V drive using a new Ge/SiGe QW epitaxy design approach; further, this is demonstrated with the thinnest Ge/SiGe epitaxy to date, using a virtual substrate only 320-nm-thick. We use an eigenmode expansion method to model the optical coupling between SOI waveguides and both vertically and butt-coupled Ge/SiGe devices, and show that this reduction in thickness is expected to lead to a significant improvement in the insertion loss of waveguide-integrated devices.
ABSTRACT
We demonstrate vertical-incidence electroabsorption modulators for free-space optical interconnects. The devices operate via the quantum-confined Stark effect in Ge/SiGe quantum wells grown on silicon substrates by reduced pressure chemical vapor deposition. The strong electroabsorption contrast enables use of a moderate-Q asymmetric Fabry-Perot resonant cavity, formed using a film transfer process, which allows for operation over a wide optical bandwidth without thermal tuning. Extinction ratios of 3.4 dB and 2.5 dB are obtained for 3 V and 1.5 V drive swings, respectively, with insertion loss less than 4.5 dB. For 60 ?m diameter devices, large signal modulation is demonstrated at 2 Gbps, and a 3 dB modulation bandwidth of 3.5 GHz is observed. These devices show promise for high-speed, low-energy operation given further miniaturization.