ABSTRACT
In this paper, glass fiber fabric reinforced polyphenylene sulfide composites were prepared by hot pressing. The effects of glass fibre modification and hot pressing temperature on the properties of the composites were investigated using a scanning electron microscope, infrared spectrometer, universal testing machine, and DIGEYE digital imaging colour measurement system. The results show that after the treatment with a silane coupling agent, the silane coupling agent was more uniformly distributed on the surface of the glass fibres, and the bonding effect between the glass fibre fabric and polyphenylene sulphide was significantly improved. The strength of the composites increased and then decreased with the increase of hot pressing temperature, and the surface colour of the composites became darker and darker. When the hot-pressing temperature is 310 °C, the mechanical properties of glass fabric-reinforced polyphenylene sulfide composites are at their best, the tensile strength reaches 51.9 MPa, and the bending strength reaches 78 MPa.
ABSTRACT
Glass fibre-reinforced polyphenylene sulphide composites were prepared by hot-pressing glass fibre fabrics and polyphenylene sulphide resins. The effects of different polyphenylene sulphide resin forms on the properties of the composites were investigated using scanning electron microscopy, dynamic mechanical analyser, pendulum impact tester and universal testing machine. The results showed that different polyphenylene sulphide resin forms had nearly no effect on the glass transition temperature of the composites, which are all located at about 100 °C. Compared with other polyphenylene sulphide composites, the bending strength of polyphenylene sulphide film composites was the highest, reaching 314.58 MPa, and the impact strength of polyphenylene sulphide particle composites was the highest, reaching 245.4 KJ/m2. The bending strength and impact strength were calculated using a standard fraction, and the highest standard fraction was obtained when the ratio of polyphenylene sulphide film to particle was 1:2. The impact strength and bending strength could be obtained. The impact strength reached 229.8 KJ/m2, and the bending strength reached 284.16 MPa.