Electrolyte Superwetting and Electrode Friendly of Porous Membrane for Better Cycling Stability of Lithium Metal Batteries.

Porous polymer membranes as separator plays important roles in separating cathode and anode, storing electrolytes, and transporting ions in energy storage devices. Here, an effective strategy is reported to prepare an electrolyte superwetting membrane, which shows good Li+ transport rate and uniformity, as well as electrode-friendly properties to afford the reduction and oxidation of electrodes. It thereby improves the cycle stability and safety of Li metal batteries. With the arrayed capillaries technique, a thin layer of polyvinylidene fluoride (PVDF) and polyacrylonitrile (PAN) composite is uniformly coated on the surface and pores of polypropylene (PP) membrane with a total thickness of 30 µm. After treating it with n-butyllithium and LiNO3 in turn, a chemically inert membrane with efficient and uniform ion transport is prepared, and the cycle stability of Li||Li symmetric cells is up to 1500 h, 4 times higher than that of PP membrane. Moreover, the Li||LiFePO4 with as-prepared membranes achieve a higher capacity retention rate of 92% after 190 cycles at a current density of 3.6 mA cm-2 and a capacity of 3.6 mAh cm-2, and the Li||NCM721 batteries achieve a capacity retention rate of 71% after 600 cycles at a current density of 1.8 mA cm-2.

Construction of Inorganic/Polymer Tandem Layer on Li Metal with Long-Term Stability by LiNO3 Concentration Gradient Electrolyte.

Metal electrode with long cycle life is decisive for the actual use of metal rechargeable batteries, while the dendrite growth and side reaction limit their cyclic stability. Herein, the construction of polymer and inorganic-rich SEI tandem layer structure on Li metal can be used for extraordinarily extending its cycle life is reported, which is generated by an in situ PVDF/LiF/LiNO3 (PLL) gel layer on the surface of Li metal with a chemically compatible ether solvent. The cycle life of Li//Li cells with the tandem layer structure is over 6000 h, six times longer than those with LiNO3 homogeneous electrolyte. It highlights the importance of LiNO3 concentration gradient electrolyte formed by the in situ PLL gel layer, in which highly concentrated LiNO3 is confined on the surface of Li metal to generate the uniform and inorganic-rich LiF/Li2O/Li3N layer on the bottom of PVDF/LiF with good mechanical strength, resulting in the dendrite free anode in cell cycling. The assembled Li//LiFePO4 and Li//NMC811 batteries show the capacity retention rate of 80.9% after 800 cycles and 82.3% after 500 cycles, respectively, much higher than those of references.