Potassic zeolites from Brazilian coal ash for use as a fertilizer in agriculture.

Brazilian coal has an ash content ranging from 30 to 50% by weight. Consequently, its use in coal-fired thermoelectric for power production generates a lot of waste. The construction sector is the largest consumer of coal ash, but it cannot absorb the entire amount generated. Thus, other applications for coal ash should be studied in aim to optimize the use of this industrial waste. This research had as focus to synthesize potassic zeolite from of the coal ash into on potassium fertilizer for the grown wheat plant. In this work, it was used a subbituminous coal from Mina do Leão (RS, Brazil) presenting 48.7% ash content on a dry basis. Concerning the synthesis of potassic zeolite, it was adopted the conventional method of hydrothermal treatment with potassium hydroxide. A schedule of experiments was conducted in order to define the optimum condition of zeolite synthesis that was then used an alkaline solution of 5M KOH with a reaction time of 24h at 150°C. According to this procedure, it was obtained a zeolite with a single crystalline phase, identified through X-ray diffraction as Merlinoite. Subsequently, it was performed a set of tests using potassic zeolite asa fertilizer for plants in a greenhouse. The synthesized potassic zeolite showed a good potential for its use as fertilizer in agriculture.

Integrated synthesis of zeolites 4A and Na-P1 using coal fly ash for application in the formulation of detergents and swine wastewater treatment.

Several researchers have reported zeolite synthesis using coal ash for a wide range of applications. However, little attention has been given to green processes, including moderate synthesis conditions, using waste as raw material and effluent reuse or reduction. In this study, Brazilian coal fly ashes were used for integrated synthesis of zeolites 4A and Na-P1 by two different routes and under moderate operating conditions (temperature and pressure). Both procedures produced zeolites with similar conversions (zeolite 4A at 82% purity and zeolite Na-P1 at 57-61%) and high CEC values (zeolites 4A: 4.5meqCa(2+)g(-1) and zeolites Na-P1: 2.6-2.8meqNH4(+)g(-1)). However, process 1 generated less effluent for the zeolite mass produced (7mLg(-1)), with low residual Si and Al levels and 74% of the Si available in the coal fly ash incorporated into the zeolite, while only 55% is used in process 2. For use as a builder in detergents, synthetic zeolite 4A exhibited conformity parameters equal to or greater than those of the commercial zeolite adopted as reference. Treatment of swine wastewater with zeolite Na-P1 resulted in a high removal capacity for total ammoniacal nitrogen (31mgg(-1)).