ABSTRACT
It is shown that substrate pixelisation before epitaxial growth can significantly impact the emission color of semiconductor heterostructures. The wavelength emission from InxGa1-xN/GaN quantum wells can be shifted from blue to yellow simply by reducing the mesa size from 90 × 90 µm2 to 10 × 10 µm2 of the patterned silicon used as the substrate. This color shift is mainly attributed to an increase of the quantum well thickness when the mesa size decreases. The color is also affected, in a lesser extent, by the trench width between the mesas. Cathodoluminescence hyperspectral imaging is used to map the wavelength emission of the InxGa1-xN/GaN quantum wells. Whatever the mesa size is, the wavelength emission is red-shifted at the mesa edges due to a larger quantum well thickness and In composition.
ABSTRACT
We demonstrate low-loss GaN/AlGaN planar waveguides grown by molecular beam epitaxy on sapphire substrates. By using a proper AlGaN cladding layer and reducing surface roughness we reach <1dB/cm propagation losses at 633nm. These low propagation losses allow an efficient second harmonic generation using modal phase matching between a TM0 pump at 1260nm and a TM2 second harmonic at 630nm. A maximal power conversion of 2% is realized with an efficiency of 0.15%·W-1cm-2. We provide a modelling that demonstrates broadband features of GaN/AlGaN platform by showing second harmonic wavelengths tunability from the visible up to the near-infrared spectral region. We discuss drawbacks of modal phase matching and propose a novel solution which allows a drastic improvement of modal overlaps with the help of a planar polarity inversion. This new approach is compatible with low propagation losses and may allow as high as 100%·W-1cm-2 conversion efficiencies in the future.