ABSTRACT
The effects on the structure and magnetic properties of Eu1-xYxMnO3 (0.0 ≤ x ≤ 0.5) thin films due to lattice strain were investigated and compared with those obtained in equivalent composition ceramics. The films were deposited by spin-coating chemical solution onto Pt\TiO2\SiO2\Si (100) standard substrates. X-ray diffraction and Raman spectroscopy measurements revealed that all films crystallize in orthorhombic structure with space group Pnma, observing an added contraction of the unit cell with increasing Y-substitution ou Eu, corresponding to a broadening of the Mn-O1-Mn angle and a gradual decrease in magnetic order response.
ABSTRACT
Changes in nominal composition of the perovskite (ABO3) solid solution Ba1-x(Zr,Pr)O3-δ and adjusted firing conditions at very high temperatures were used to induce structural changes involving site redistribution and frozen-in point defects, as revealed by Raman and photoluminescence spectroscopies. Complementary magnetic measurements allowed quantification of the reduced content of Pr. Weak dependence of oxygen stoichiometry with temperature was obtained by coulometric titration at temperatures below 1000 °C, consistent with a somewhat complex partial frozen-in defect chemistry. Electrical conductivity measurements combined with transport number and Seebeck coefficient measurements showed prevailing electronic transport and also indicated trends expected for partial frozen-in conditions. Nominal Ba deficiency and controlled firing at very high temperatures allows adjustment of structure and partial frozen-in defect chemistry, opening the way to engineer relevant properties for high-temperature electrochemical applications.