ABSTRACT
The present study reveals the microstructural evolution and corresponding mechanisms occurring during different stages of quenching and partitioning (Q&P) conducted on 0.6C-1.5Si steel using in-situ High Energy X-Ray Diffraction (HEXRD) and high-resolution dilatometry methods. The results support that the symmetry of ferrite is not cubic when first formed since it is fully supersaturated with carbon at the early stages of partitioning. Moreover, by increasing partitioning temperature, the dominant carbon source for austenite enrichment changes from ongoing bainitic ferrite transformation during the partitioning stage to initial martensite formed in the quenching stage. At low partitioning temperatures, a bimodal distribution of low- and high-carbon austenite, 0.6 and 1.9 wt.% carbon, is detected. At higher temperatures, a better distribution of carbon occurs, approaching full homogenization. An initial martensite content of around 11.5 wt.% after partitioning at 280 °C via bainitic ferrite transformation results in higher carbon enrichment of austenite and increased retained austenite amount by approximately 4% in comparison with partitioning at 500 °C. In comparison with austempering heat treatment with no prior martensite, the presence of initial martensite in the Q&P microstructure accelerates the subsequent low-temperature bainitic transformation.
ABSTRACT
Laser powder bed fusion (L-PBF) has attracted great interest in the aerospace and medical sectors because it can produce complex and lightweight parts with high accuracy. Austenitic stainless steel alloy 316 L is widely used in many applications due to its good mechanical properties and high corrosion resistance over a wide temperature range. In this study, L-PBF-processed 316 L was investigated for its suitability in aerospace applications at cryogenic service temperatures and the behavior at cryogenic temperature was compared with room temperature to understand the properties and microstructural changes within this temperature range. Tensile tests were performed at room temperature and at -196 °C to study the mechanical performance and phase changes. The microstructure and fracture surfaces were characterized using scanning electron microscopy, and the phases were analyzed by X-ray diffraction. The results showed a significant increase in the strength of 316 L at -196 °C, while its ductility remained at an acceptable level. The results indicated the formation of ε and α martensite during cryogenic testing, which explained the increase in strength. Nanoindentation revealed different hardness values, indicating the different mechanical properties of austenite (γ), strained austenite, body-centered cubic martensite (α), and hexagonal close-packed martensite (ε) formed during the tensile tests due to mechanical deformation.
ABSTRACT
The effect of ultrasonic treatment on the microstructural evolution and the related softening process in tensile pre-deformed 316 stainless steel was studied by means of electron backscatter diffraction method, optical microscopy, and microhardness measurement. It was observed that different levels of ultrasonic energy induced complex microstructural changes in the treated samples. A large decrease in twin boundaries was observed, which is an indication of the de-twinning process under ultrasonic treatment. A new mechanism for the de-twinning process under oscillatory stress of ultrasonic vibration was proposed. It was shown that de-twinning under ultrasonic treatment led to dislocation production from twin boundaries. Inverse pole figures investigation revealed strong grain rotation following ultrasonic treatment in tensile pre-deformed samples. Subgrain formation in the ultrasonic treated austenitic stainless steel samples indicated that considerable ultrasonic energy was induced by the ultrasonic vibration, which provided the activation energy needed for dislocation climb and cross-slip. The ultrasonic induced subgrain formation, dislocation annihilation, and de-twinning, which resulted in a decrease of the microhardness in the samples, can be considered as possible mechanisms for the acoustic softening in the austenitic stainless steels.
ABSTRACT
The aim of this work was to investigate the microstructure and the mechanical properties of laser-welded joints combined of Dual Phase DP800 and DP1000 high strength thin steel sheets. Microstructural and hardness measurements as well as tensile and fatigue tests have been carried out. The welded joints (WJ) comprised of similar/dissimilar steels with similar/dissimilar thickness were consisted of different zones and exhibited similar microstructural characteristics. The trend of microhardness for all WJs was consistent, characterized by the highest value at hardening zone (HZ) and lowest at softening zone (SZ). The degree of softening was 20 and 8% for the DP1000 and DP800 WJ, respectively, and the size of SZ was wider in the WJ combinations of DP1000 than DP800. The tensile test fractures were located at the base material (BM) for all DP800 weldments, while the fractures occurred at the fusion zone (FZ) for the weldments with DP1000 and those with dissimilar sheet thicknesses. The DP800-DP1000 weldment presented similar yield strength (YS, 747 MPa) and ultimate tensile strength (UTS, 858 MPa) values but lower elongation (EI, 5.1%) in comparison with the DP800-DP800 weldment (YS 701 MPa, UTS 868 MPa, EI 7.9%), which showed similar strength properties as the BM of DP800. However, the EI of DP1000-DP1000 weldment was 1.9%, much lower in comparison with the BM of DP1000. The DP800-DP1000 weldment with dissimilar thicknesses showed the highest YS (955 MPa) and UTS (1075 MPa) values compared with the other weldments, but with the lowest EI (1.2%). The fatigue fractures occurred at the WJ for all types of weldments. The DP800-DP800 weldment had the highest fatigue limit (348 MPa) and DP800-DP1000 with dissimilar thicknesses had the lowest fatigue limit (<200 MPa). The fatigue crack initiated from the weld surface.