ABSTRACT
The fabrication of bi-material micro-components via two-component micro-powder injection moulding (2C-µPIM) from 3 mol% yttria-stabilised zirconia (3YSZ) and micro/nano bimodal stainless steel 316L (SS 316L) powders has received insufficient attention. Apart from this, retaining the bonding between ceramic and metal at different processing stages of 2C-µPIM is challenging. This study investigated the solvent and thermal debinding mechanisms of green bi-material micro-parts of 3YSZ and bimodal SS 316L without collapsing the ceramic/metal joining. In this research, feedstocks were prepared by integrating the powders individually with palm stearin and low-density polyethylene binders. The results demonstrated that during the solvent debinding process, the palm stearin removal rate in the bi-materials composed of 3YSZ and bimodally configured SS 316L feedstocks intensified with an increase in temperature. The establishment of interconnected pores in the solvent-debound components facilitated the thermal debinding process, which removed 99% of the binder system. Following sintering, the debound bi-materials exhibited a relative density of 95.3%. According to a study of the microstructures using field emission scanning electron microscopy, an adequate bond between 3YSZ and bimodal SS 316L was established in the micro-part after sintering. The bi-material sintered at 1350 °C had the highest hardness of 1017.4 HV along the joining region.
ABSTRACT
Metal injection molding (MIM) is one of the most widely used manufacturing processes worldwide as it is a cost-effective way of producing a variety of dental and orthopedic implants, surgical instruments, and other important biomedical products. Titanium (Ti) and Ti alloys are popular modern metallic materials that have revamped the biomedical sector as they have superior biocompatibility, excellent corrosion resistance, and high static and fatigue strength. This paper systematically reviews the MIM process parameters that extant studies have used to produce Ti and Ti alloy components between 2013 and 2022 for the medical industry. Moreover, the effect of sintering temperature on the mechanical properties of the MIM-processed sintered components has been reviewed and discussed. It is concluded that by appropriately selecting and implementing the processing parameters at different stages of the MIM process, defect-free Ti and Ti alloy-based biomedical components can be produced. Therefore, this present study could greatly benefit future studies that examine using MIM to develop products for biomedical applications.
ABSTRACT
The production of fabricated filaments for fused deposited modelling printing is critical, especially when higher loading filler (>20 wt.%) is involved. At higher loadings, printed samples tend to experience delamination, poor adhesion or even warping, causing their mechanical performance to deteriorate considerably. Hence, this study highlights the behaviour of the mechanical properties of printed polyamide-reinforced carbon fibre at a maximum of 40 wt.%, which can be improved via a post-drying process. The 20 wt.% samples also demonstrate improvements of 500% and 50% in impact strength and shear strength performance, respectively. These excellent performance levels are attributed to the maximum layup sequence during the printing process, which reduces the fibre breakage. Consequently, this enables better adhesion between layers and, ultimately, stronger samples.