Polariton Condensation in Gap-Confined States of Photonic Crystal Waveguides.

The development of patterned multiquantum well heterostructures in GaAs/AlGaAs waveguides has recently made it possible to achieve exciton-polariton condensation in a topologically protected bound state in the continuum (BIC). Polariton condensation was shown to occur above a saddle point of the two-dimensional polariton dispersion in a one-dimensional photonic crystal waveguide. A rigorous analysis of the condensation phenomenon in these systems, as well as the role of the BIC, is still missing. In the present Letter, we theoretically and experimentally fill this gap by showing that polariton confinement resulting from the negative effective mass and the photonic energy gap in the dispersion play a key role in enhancing the relaxation toward the condensed state. In fact, our results show that low-threshold polariton condensation is achieved within the effective trap created by the exciting laser spot, regardless of whether the resulting confined mode is long-lived (polariton BIC) or short-lived (lossy mode). In both cases, the spatial quantization of the polariton condensate and the threshold differences associated to the corresponding state lifetime are measured and characterized. For a given negative mass, a slightly lower condensation threshold from the polariton BIC mode is found and associated to its reduced radiative losses, as compared to the lossy one.

Excitonic absorption and defect-related emission in three-dimensional MoS2 pyramids.

MoS2 micro-pyramids have demonstrated interesting properties in the fields of photonics and non-linear optics. In this work, we show the excitonic absorption and cathodoluminescence (CL) emission of MoS2 micro-pyramids grown by chemical vapor deposition (CVD) on SiO2 substrates. The excitonic absorption was obtained at room and cryogenic temperatures by taking advantage of the cathodoluminescence emission of the SiO2 substrate. We detected the CL emission related to defect intra-gap states, localized at the pyramid edges and with an enhanced intensity at the pyramid basal vertices. The photoluminescence and absorption analysis provided the Stokes shift of both the A and B excitons in the MoS2 pyramids. This analysis provides new insights into the optical functionality of MoS2 pyramids. This method can be applied to other 3D structures within the 2D materials family.