Temperature increase at the light guide tip of 15 contemporary LED units and thermal variation at the pulpal floor of cavities: an infrared thermographic analysis.

In this study, a comprehensive investigation on the temperature increase at the light guide tip of several commercial light-emitting diode (LED) light-curing units (LCUs) and the associated thermal variation (ΔT) at the pulpal floor of dental cavities was carried out. In total, 15 LEDs from all generations were investigated, testing a quartz-tungsten-halogen (QTH) unit as a reference. The irradiance level was measured with a power meter, and spectral distribution was analyzed using a spectrometer. Temperature increase at the tip was measured with a type-K thermocouple connected to a thermometer, while ΔT at the pulpal floor was measured by an infrared photodetector in class V cavities, with a 1-mm-thick dentin pulpal floor. The relationship among measured irradiance, ΔT at the tip, and ΔT at the pulpal floor was investigated using regression analyses. Large discrepancies between the expected and measured irradiances were detected for some LCUs. Most of the LCUs showed an emission spectrum narrower than the QTH unit, with emission peaks usually between 450 and 470 nm. The temperature increase at the tip followed a logarithmic growth for LCUs with irradiance ≥1000 mW/cm(2), with ΔT at the tip following the measured irradiance linearly (R(2)=0.67). Linear temperature increase at the pulpal floor over the 40-second exposure time was observed for several LCUs, with linear association between ΔT at the pulpal floor and measured irradiance (R(2)=0.39) or ΔT at the tip (R(2)=0.28). In conclusion, contemporary LED units show varied irradiance levels that affect the temperature increase at the light guide tip and, as a consequence, the thermal variation at the pulpal floor of dental cavities.

Influence of photoactivation protocol and light guide distance on conversion and microleakage of composite restorations.

PURPOSE: To evaluate the effect of light guide distance and the different photoactivation methods on the degree of conversion (DC) and microleakage of a composite. METHODS AND MATERIALS: Three photoactivation protocols (600 mW/cm2 x 40 seconds; 400 mW/cm2 x 60 seconds or 200 mW/cm2 x 20 seconds, followed by 500 mW/cm2 x 40 seconds) and three distances from the light source (0, 3 or 7 mm) were tested. Cylindrical specimens (5 mm diameter; 2 mm tall; n=3) were prepared for the DC test (FT-Raman). Class V cavities were made in 90 bovine incisors to conduct the microleakage test. The specimens were conditioned for 15 seconds with phosphoric acid (37%), followed by application of the adhesive system Prime & Bond NT (Dentsply/Caulk). The preparations were restored in bulk. The specimens were stored for 24 hours in distilled water (37 degrees C) before being submitted to the silver-nitrate microleakage protocol. The restorations were sectioned and analyzed under 25x magnification. RESULTS: Statistical analyses (two-way ANOVAs and Tukey test, alpha=0.05) found significance only for the factor distance (p=0.015) at the top of the composite for the DC test. Conversion was statistically lower for the 7 mm groups compared to the 0 and 3 mm groups, which were equivalent to each other. At the bottom of the specimens, none of the factors or interactions was significant (p<0.05). The Kruskal-Wallis test showed that, in general, the soft-start method led to lower microleakage scores when compared to the continuous modes, mainly when associated with a distancing of 7 mm (p<0.01). With the exception of specimens irradiated with 400 mW/cm2 that did not demonstrate variations on scores for the distances tested, higher microleakage was observed for shorter distances from the light source. CONCLUSIONS: Soft-start methods may reduce microleakage when the light guide distancing provides a low level of irradiance, which also causes a discrete reduction in the DC.