ABSTRACT
As an efficient non-precious metal catalyst for the oxygen evolution reaction (OER), phosphides suffer from poor electrical conductivity, so it is still a challenge to reasonably design their structures to further improve their conductivity and OER performances. Here, we present a novel Ni5P4/N-doped carbon@CoFeP/N-doped carbon composite (Ni5P4/NC@CoFeP/NC) as electrocatalysts for OER. This elaborate structure consists of Ni5P4/NC derived from Ni-MOF and CoFeP/NC derived from CoFe-Prussian blue analog MOF (Co-Fe PBA). The cube-like CoFeP/NC are scattered and uniformly coated on the sheet of Ni5P4/NC flowers. Among them, NC can enhance the conductivity of phosphides, while CoFeP/NC can increase the electrochemical active area, which benefit the properties of Ni5P4/NC@CoFeP/NC. Notably, the Ni5P4/NC@CoFeP/NC catalyst possesses outstanding OER performances with a low overpotential of 260 and 303 mV at a current density of 10 and 100 mA·cm-2, an ultra-low Tafel slope of 31.1 mV·dec-1 and excellent stability in 1 M KOH. XPS analysis shows that proper chemical composition promotes the oxidation of transition metal species and the chemisorption of OH-, thus accelerating the OER kinetics. Therefore, this work provides a hopeful method for designing and preparing transition metal phosphide/carbon composite as OER electrocatalysts.
ABSTRACT
Metal-organic-frameworks (MOFs) derived carbon or nitrogen-doped carbon (NC) materials are usually used as electromagnetic wave (EMW) absorbers. However, the effective control of the composition and structure of composites is still a major challenge for the development of high-performance EMW absorbing materials. In this work, core-shell structure and bimetallic composition Cu/nitrogen doped carbon @Co/ nitrogen doped carbon (Cu/NC@Co/NC) composites were designed and synthesized through the thermal decomposition of Cu-MOF@Co-MOF precursor. Cu/NC@Co/NC composites with different compositions were obtained by changing the ratio of Co-MOF and Cu-MOF. The composite (Cu/NC@Co/NC-3.75) prepared using 3.75 mmol of Co(NO3)2·6H2O exhibits outstanding EMW absorption properties due to the optimized impedance matching and strong attenuation ability, which is caused by enhanced interfacial and dipolar polarization as well as multiple reflection and scattering. With the filler loading in paraffin of 35 wt%, the minimum reflection loss (RLmin) is up to -54.13 dB at 9.84 GHz with a thin thickness of 3 mm, and the effective absorption bandwidth (EAB, RL≤ - 10 dB) reaches 5.19 GHz (10.18-15.37 GHz) with the corresponding thickness of 2.5 mm. Compared with the Cu/NC and Co/NC, the Cu/NC@Co/NC-3.75 composite exhibits much better EMW absorbing performances caused by the bimetallic composition and the unique core-shell structure. This work provides a rational design for MOF-derived lightweight and broadband EMW absorbing materials.
ABSTRACT
Developing lightweight and broadband microwave absorbers for dealing with serious electromagnetic radiation pollution is a great challenge. Here, a novel Fe-Co/N-doped carbon/reduced graphene oxide (Fe-Co/NC/rGO) composite with hierarchically porous structure was designed and synthetized by in situ growth of Fe-doped Co-based metal organic frameworks (Co-MOF) on the sheets of porous cocoon-like rGO followed by calcination. The Fe-Co/NC composites are homogeneously distributed on the sheets of porous rGO. The Fe-Co/NC/rGO composite with multiple components (Fe/Co/NC/rGO) causes magnetic loss, dielectric loss, resistance loss, interfacial polarization, and good impedance matching. The hierarchically porous structure of the Fe-Co/NC/rGO enhances the multiple reflections and scattering of microwaves. Compared with the Co/NC and Fe-Co/NC, the hierarchically porous Fe-Co/NC/rGO composite exhibits much better microwave absorption performances due to the rational composition and porous structural design. Its minimum reflection loss (RLmin) reaches - 43.26 dB at 11.28 GHz with a thickness of 2.5 mm, and the effective absorption frequency (RL ≤ - 10 dB) is up to 9.12 GHz (8.88-18 GHz) with the same thickness of 2.5 mm. Moreover, the widest effective bandwidth of 9.29 GHz occurs at a thickness of 2.63 mm. This work provides a lightweight and broadband microwave absorbing material while offering a new idea to design excellent microwave absorbers with multicomponent and hierarchically porous structures.