A new designed π conjugated molecule for stable single walled carbon nanotube dispersion in aqueous medium.

A molecule with a π conjugated backbone built from aromatic thiophene and dialkoxyphenylene units and substituted imidazolium groups (TPO) is designed to obtain ultra-stable single walled carbon nanotube (SWCNT) dispersion in aqueous medium. The proposed mechanism of non-covalent interaction is accompanied by individualization of SWCNT and comprises of dominant nondisruptive π-π and cation-π interaction between them and the TPO conjugated oligomer. The individualization of SWCNT and dispersibility and stability of the ultra-stable suspensions were estimated using high resolution transmission electron microscopy, UV-Visible-NIR absorption spectroscopy, Raman spectroscopy, photoluminescence and zeta potential measurement. Nuclear magnetic resonance data provides direct evidence toward possible cation-π interaction.

The influence of oxygen-containing functional groups on the dispersion of single-walled carbon nanotubes in amide solvents.

Surface composition plays an important role in carbon nanotube dispersibility in different environments. Indeed, it determines the choice of dispersion medium. In this paper the effect of oxidation on the dispersion of HiPCO single-walled carbon nanotubes (SWNTs) in N-methyl-pyrrolidinone (NMP), N,N-dimethylformamide (DMF), N,N-dimethylacetamide (DMA), N-dodecyl-pyrrolidinone (N12P) and cyclohexyl-pyrrolidinone (CHP) was systematically studied. During the oxidation process, similar amounts of carboxylic acid and phenolic groups were introduced to mostly already existing defects. For each solvent the dispersion limits and the absorption coefficients were estimated by optical absorption analysis over a range of SWNT concentrations. The presence of acid oxygenated groups increased SWNT dispersibility in NMP, DMF and DMA, but decreased in N12P and CHP. The absorption coefficients, however, decreased for all solvents after oxidation, reflecting the weakening of the effective transition dipole of the π-π transition with even limited extension functionalization and solvent interaction. The analysis of the results in terms of Hansen and Flory-Huggins solubility parameters evidenced the influence of dipolar interactions and hydrogen bonding on the dispersibility of oxidized SWNTs.

Decarboxylation of oxidized single-wall carbon nanotubes.

A classical protocol widely used in organic chemistry of aromatic and polyaromatic molecules has been successfully applied in this work for the decarboxylation of oxidized single-wall carbon nanotube (SWNT) to rend C-H SWNT derivatives. SWNT produced by arc discharge method have been oxidized during a purification process using strongly oxidant agents, such as hydrogen peroxide and nitric acid. The decarboxylation of oxidized SWNT has been conduced with copper(I) oxide in a 50:50 solution of N-methylpyrrolidone and quinoline. Fourier transform infrared spectroscopy, X-ray photoelectron spectroscopy and acid-base potentiometric titration analyses were carried out to characterize quali and quantitatively the changes in the chemical environment on the SWNT surface in each step of the purification and the decarboxylation process. Those techniques showed the appearance of mainly carboxylic and phenolic groups after the purification process and the disappearance of the carboxylic groups after the decarboxylation reaction. Fourier transform infrared spectroscopy analysis indicated also the formation of aliphatic and aromatic C-H groups. X-ray photoelectron spectroscopy and potentiometric titration results determined an efficiency higher than 90% for our decarboxylation procedure. The purity and structural quality of the SWNT sample used in the decarboxylation process were evaluated by thermogravimetry and Raman spectroscopy. Thermogravimetric analysis identified a purified sample with approximately 80 wt% of SWNT, in fractions distributed in highly structured SWNTs (25 wt%), with distribution in composition, length and structural quality (35 wt%) and with very defective and short tubes (25 wt%). The damages on the purified SWNT walls were characterized by the Raman scattering analysis.

Infrared-active vibrational modes of single-walled carbon nanotubes.

The IR-active vibrational modes of single-walled carbon nanotubes have been observed by optical transmission through thin films of bundled nanotubes. Because IR-active chemical functional groups, e.g., -COOH, -OH, might be attached to the tube walls and contribute additional spectral features, we have also studied the effects of chemical purification and long-term high-temperature vacuum annealing on the IR spectrum. Through comparison with theory, we are able to assign much of the sharp structure observed in our IR spectra.

Debundling and dissolution of single-walled carbon nanotubes in amide solvents.

Wet chemical methods involving ultrasound and amide solvents were used to purify and separate large bundles of single-walled carbon nanotubes (SWNTs) into individual nanotubes that could then be transported to silicon or mica substrates. The SWNTs studied were produced by the arc-discharge process. Dry oxidation was used in an initial step to remove amorphous carbon. Subsequently, two acid purification schemes were investigated (HCl- and HNO(3)-reflux) to remove the metal growth catalyst (Ni-Y). Finally, ultrasonic dispersion of isolated tubes into either N,N-dimethylformamide (DMF) or N-methyl-2-pyrrolidone (NMP) was carried out. Raman scattering, atomic force microscopy (AFM), and electron microscopy were used to study the evolution of the products. Raman scattering was used to probe possible wall damage during the chemical processing. We found that both HCl and HNO(3) could be used to successfully remove the Ni-Y below approximately 1 wt %. However, the HNO(3)-reflux produced significant wall damage (that could be reversed by vacuum annealing at 1000 degrees C). In the dispersion step, both amide solvents (DMF and NMP) produced a high degree of isolated tubes in the final product, and no damage during this dispersion step was observed. HNO(3)-refluxed tubes were found to disperse the best into the amide solvents, perhaps because of significant wall functionalization. AFM was used to study the filament diameter and length distributions in the final product, and interesting differences in these distributions were observed, depending on the chemical processing route.