1.
Polymers (Basel) ; 15(13)2023 Jun 26.
Article in English | MEDLINE | ID: mdl-37447463

ABSTRACT

In this study, composites containing polylactide and carbonate lake sediment in concentrations of 2.5, 5, 10, and 15% by weight were prepared by a 3D printing method. The material for 3D printing was obtained by directly diluting the masterbatch on an injection moulder to the desired concentrations, and after granulation, it was extruded into a filament. The material prepared thusly was used to print standardised samples for mechanical testing. To compare the mechanical properties of the composites obtained by 3D printing and injection moulding, two sets of tests were performed, i.e., mechanical tests (tensile strength, flexural strength, and impact strength) and hydrophobic-hydrophilic surface character testing. The degree of composite waste in the 3D printing was also calculated. Mechanical and surface tests were performed for both systems conditioned at room temperature and after accelerated ageing in a weathering chamber. The study showed differences in the properties of composites obtained by 3D printing. Sedimentary fillers improved the hydrophobicity of the systems compared with pure PLA, but it was not a linear relationship. The PLA/CLS sedB composite had higher strength parameters, especially after ageing in a weathering chamber. This is due to its composition, in which, in addition to calcite and silica, there are also aluminosilicates, causing a strengthening of the PLA matrix.

2.
Biomimetics (Basel) ; 8(2)2023 Jun 03.
Article in English | MEDLINE | ID: mdl-37366830

ABSTRACT

Structural bioinspiration in modern material science and biomimetics represents an actual trend that was originally based on the bioarchitectural diversity of invertebrate skeletons, specifically, honeycomb constructs of natural origin, which have been in humanities focus since ancient times. We conducted a study on the principles of bioarchitecture regarding the unique biosilica-based honeycomb-like skeleton of the deep-sea glass sponge Aphrocallistes beatrix. Experimental data show, with compelling evidence, the location of actin filaments within honeycomb-formed hierarchical siliceous walls. Principles of the unique hierarchical organization of such formations are discussed. Inspired by poriferan honeycomb biosilica, we designed diverse models, including 3D printing, using PLA-, resin-, and synthetic-glass-prepared corresponding microtomography-based 3D reconstruction.

3.
Polymers (Basel) ; 15(6)2023 Mar 21.
Article in English | MEDLINE | ID: mdl-36987343

ABSTRACT

Amorphic diatomaceous earth is derived from natural sources, and polyamide 11 (PA11) is produced from materials of natural origin. Both of these materials show a low harmfulness to the environment and a reduced carbon footprint. This is why the combination of these two constituents is beneficial not only to improve the physicochemical and mechanical properties of polyamide 11 but also to produce a biocomposite. For the purpose of this paper, the test biocomposite was produced by combining polyamide 11, as well as basic and pre-fractionated diatomaceous earth, which had been subjected to silanization. The produced composites were used to carry out rheological (melt flow rate-MFR), mechanical (tensile strength, bending strength, impact strength), crystallographic (X-ray Diffraction-XRD), thermal and thermo-mechanical (differential scanning calorimetry-DSC, dynamic mechanical thermal analysis-DMTA) analyses, as well as a study of hydrophobic-hydrophilic properties of the material surface (wetting angle) and imaging of the surface of the composites and the fractured specimens. The tests showed that the additive 3-aminopropyltriethoxysilane (APTES) acted as an agent that improved the elasticity of composites and the melt flow rate. In addition, the produced composites showed a hydrophilic surface profile compared to pure polylactide and polyamide 11.

4.
Sci Rep ; 13(1): 1161, 2023 Jan 20.
Article in English | MEDLINE | ID: mdl-36670202

ABSTRACT

In this study, injection moulding was applied to produce biocomposites consisting of polylactide (PLA) and amorphous diatomaceous earth used as a filler at different concentrations. Natural wax and synthetic wax were added to improve processing properties, comparing the resulting biocomposites. The use of natural beeswax makes the composite environmentally friendly. The prepared composites contained 2.5, 5, 10 and 15% w/w filler. The test samples have been injection moulded. Rheological, mechanical, surface and other properties were assessed for the fabricated composites. The testing has shown that the use of wax additives has a significant influence on the mechanical properties (tensile strength, flexural strength, impact strength) and the hydrophilicity/hydrophobicity of composite surfaces. The addition of natural wax, especially at lower concentration, has a positive effect on the rheological properties of composites (melt flow rate, MFR), flexural modulus and impact strength. Different composite parameters are modified by different wax types so both natural and synthetic waxes, can be used interchangeably, depending on the required final material characteristics.

5.
Polymers (Basel) ; 14(24)2022 Dec 15.
Article in English | MEDLINE | ID: mdl-36559860

ABSTRACT

In this study, the influence of TiO2 pigment filler modified with spherosilicate derivatives on the processes and thermomechanical properties of composites based on PLA was investigated. Rheological tests (MFR) were carried out, on the basis of which it was found that the addition of organosilicon compounds has a plasticizing effect on the polymer-filler systems. TGA and DSC analysis were performed. The analysis of the contact angle showed that 1.5% of the additives had an influence on the superhydrophobic properties of TiO2 (above 135°), and a slight improvement of this parameter was also observed for composites containing the modified pigment. Microscopic analysis and mechanical tests (tensile strength, impact strength and flexural strength tests) were carried out as well. It has been observed that the addition of certain derivatives adversely affects the dispersion of the filler, thus a slight improvement in mechanical properties is observed. For modifiers that do not affect filler agglomeration, a plasticizing effect on the composite is observed.

6.
Polymers (Basel) ; 14(24)2022 Dec 16.
Article in English | MEDLINE | ID: mdl-36559878

ABSTRACT

In the present study, tests were conducted on high-filled composite samples on a polylactide matrix, modified with diatomaceous earth, three types of silanes, and natural and synthetic wax. The obtained samples were characterized in terms of the effect of modifications on mechanical properties (tensile strength, flexural strength, and impact resistance) or processing properties, e.g., melt flow rate (MFR). The study showed that the modification had a favorable effect on the processing properties of the composites, associated with up to an eight-fold increase in flow rate index compared with the reference sample, especially for samples treated with methyltrimethoxysilane (MTMOS), and up to a ten-fold increase under low shear-rate flow conditions. The effect of the addition of waxes of different origins (synthetic and natural) was also determined, and it was shown that beeswax tended to reduce the flow rate of the composites regardless of the silane used. The addition of synthetic wax to composites increased the tendency to agglomerate diatomaceous earth, while natural wax had a positive effect on filler dispersion.

7.
Materials (Basel) ; 15(17)2022 Sep 02.
Article in English | MEDLINE | ID: mdl-36079485

ABSTRACT

In this study, the influence of carbonate lake sediments (Polylactide/Carbonate Lake Sediments-PLA/CLS) on the mechanical and structural properties of polylactide matrix composites was investigated. Two fractions of sediments originating from 3-8 and 8-12 m were analysed for differences in particle size by distribution (Dynamic Light Scattering-DLS), phase composition (X-ray Diffraction-XRD), the presence of surface functional groups (Fourier Transform-Infrared-FT-IR), and thermal stability (Thermogravimetric Analysis-TGA). Microscopic observations of the composite fractures were also performed. The effect of the precipitate fraction on the mechanical properties of the composites before and after conditioning in the weathering chamber was verified through peel strength, flexural strength, and impact strength tests. A melt flow rate study was performed to evaluate the effect of sediment on the processing properties of the PLA/CLS composite. Hydrophobic-hydrophilic properties were also investigated, and fracture analysis was performed by optical and electron microscopy. The addition of carbon lake sediments to PLA allows for the obtention of composites resistant to environmental factors such as elevated temperature or humidity. Moreover, PLA/CLS composites show a higher flow rate and higher surface hydrophobicity in comparison with unmodified PLA.

8.
Polymers (Basel) ; 14(15)2022 Aug 02.
Article in English | MEDLINE | ID: mdl-35956665

ABSTRACT

Amorphous diatomite was used as a filler for a thermoplastic polymer of polyamide 11 obtained from natural sources. The diatomite particles of different sizes were previously fractionated by sedimentation to obtain powders with varying particle size distribution, including powders with or without frustule particles, crushed, uncrushed or agglomerated. Biocomposites containing 2.5, 5, 10 and 20% filler were tested for their mechanical properties, including tensile strength, flexural strength and impact strength. In addition, a particle size analysis (by Dynamic Light Scattering, DLS) was performed and the dispersion of the filler in the polymer matrix (Scanning Electron Microscopy, SEM), thermal parameters (Differential Scanning Calorimetry, DSC, and Dynamic Mechanical Analysis, DMA) were determined. Testing showed that biocomposites modified with diatomaceous earth have a higher mechanical strength than the reference system, especially with larger amounts of the filler (10 and 20%), e.g., the tensile strength of pure PA11 is about 46 MPa, while 20OB and 20OF 47.5 and 47 MPa, respectively, while an increase in max. flexural strength and flexural modulus is also observed compared to pure PA11 by a maximum of 63 and 54%, respectively Diatomaceous earth can be obtained in various ways-it is commercially available or it is possible to breed diatoms in laboratory conditions, while the use of commercially available diatomite, which contains diatoms of different sizes, eliminates the possibility of controlling mechanical parameters by filling biocomposites with a filler with the desired particle size distribution, and diatom breeding is not possible on an industrial scale. Our proposed biocomposite based on fractionated diatomaceous earth using a sedimentation process addresses the current need to produce biocomposite materials from natural sources, and moreover, the nature of the process, due to its simplicity, can be successfully used on an industrial scale.