Chitosan-laponite nanocomposite scaffolds for wound dressing application.

The pivotal issue of skin regeneration research is the development of effective biomaterials that exhibit biological activities as fungicide and bactericide, combining simple and low cost manufacturing technologies. In this context, nanocomposite scaffolds based on chitosan (Ch)/Laponite (Lap) were produced by using different concentrations of Lap via freeze-drying process for potential application in skin regeneration. The influence of Lap concentration on the scaffold properties was evaluated. The prepared scaffolds were characterized by x-ray diffraction (XRD), scanning electron microscopy (SEM), porosity, swelling capacity, and mechanical analyses. The results revealed that the scaffolds exhibited a porous architecture, besides the increase in the clay content, leads to an increase in the porosity, an improvement of mechanical strength, and a decrease of swelling capacity. In vitro tests were also carried out to evaluate the biocompatibility of the materials, such as bioadhesion, antibacterial activity, viability, and cell adhesion. Viability and cell adhesion demonstrated that all scaffolds were not cytotoxic and the fibroblast cells readily attached on the surface of the scaffolds. Thereby, the results suggested that the nanocomposite scaffolds are biomaterials potentially useful as wound dressings.

Photochemical synthesis of silver nanoparticles on chitosans/montmorillonite nanocomposite films and antibacterial activity.

Silver nanoparticles (AgNPs) were synthetized on chitosans/montmorillonite nanocomposite films by photochemical method. Nanocomposites were prepared using chitosans with different molar masses and deacetylation degrees, as well as modified with diethylaminoethyl (DEAE) and dodecyl groups. AgNPs formation on the films was followed by the appearance of the plasmon band around 440nm as a function of irradiation time. TEM images revealed AgNPs with spherical morphology for all nanocomposites. For nanocomposites using modified chitosans, the AgNPs synthesis occurred quickly (1.5h) while for the others films it was above 11h. The film of modified chitosan with dodecyl and DEAE groups presented smaller and more uniform nanoparticles size along mixture of exfoliated and intercalated structures. This modified chitosan is an amphiphilic compound that can act controlling the size/shape of the AgNPs. The results of antibacterial activity suggested that all nanocomposite-AgNPs films inhibited the growth of Escherichia coli and Bacillus subtilis.