Electronic transport properties of the Al0.5TiZrPdCuNi alloy in the high-entropy alloy and metallic glass forms.

High-entropy alloys (HEAs) are characterized by a simultaneous presence of a crystal lattice and an amorphous-type chemical (substitutional) disorder. In order to unravel the effect of crystal-glass duality on the electronic transport properties of HEAs, we performed a comparative study of the electronic transport coefficients of a 6-component alloy Al0.5TiZrPdCuNi that can be prepared either as a HEA or as a metallic glass (MG) at the same chemical composition. The HEA and the MG states of the Al0.5TiZrPdCuNi alloy both show large, negative-temperature-coefficient resistivity, positive thermopower, positive Hall coefficient and small thermal conductivity. The transport coefficients were reproduced analytically by the spectral conductivity model, using the Kubo-Greenwood formalism. For both modifications of the material (HEA and MG), contribution of phonons to the transport coefficients was found small, so that their temperature dependence originates predominantly from the temperature dependence of the Fermi-Dirac function and the variation of the spectral conductivity and the related electronic density of states with energy within the Fermi-level region. The very similar electronic transport coefficients of the HEA and the MG states point towards essential role of the immense chemical disorder.

The Effect of Scandium on the Structure, Microstructure and Superconductivity of Equimolar Sc-Hf-Nb-Ta-Ti-Zr Refractory High-Entropy Alloys.

In this study, we investigate the scandium-containing Sc-Hf-Nb-Ta-Ti-Zr system of refractory high-entropy alloys (HEAs). Using the arc-melting method, we synthesized nine equimolar alloys (five 4-, three 5- and one 6-component), with all of them containing Sc. The alloys were characterized by XRD, electron microscopy and EDS, while superconductivity was investigated via electrical resistivity, specific heat and the Meissner effect. The results were compared to the parent Hf-Nb-Ta-Ti-Zr refractory HEAs, forming a single-phase body-centered cubic (bcc) structure and quite homogeneous microstructure. The addition of Sc produces a two-phase structure in the Sc-Hf-Nb-Ta-Ti-Zr alloys, with one phase being bcc and the other hexagonal close-packed (hcp). The hcp phase absorbs practically all Sc, whereas the Sc-poor bcc phase is identical to the bcc phase in the Hf-Nb-Ta-Ti-Zr parent system. Upon the Sc addition, the microstructure becomes very inhomogeneous. Large bcc dendrites (10-100 µm) are homogeneous in the central parts, but become a fine dispersion of sub-micron precipitates of the bcc and hcp phases close to the edges. The interdendritic regions are also a fine dispersion of the two phases. Superconductivity of the Sc-Hf-Nb-Ta-Ti-Zr alloys originates from the bcc phase fraction, which demonstrates identical superconducting parameters as the bcc Hf-Nb-Ta-Ti-Zr parent alloys, while the Sc-containing hcp phase fraction is non-superconducting.

Structure and Spin-Glass Magnetism of the MnxNi2Zn11-x Pseudobinary γ-Brasses at Low Mn Contents.

The pseudobinary MnxNi2Zn11-x γ-brass-type phases at low Mn dopant levels (x = 0.1-0.5) were investigated. Crystal structures were determined for the two loading compositions of x = 0.3 and 0.5. The structures were solved in the cubic space group of I43m and are described in close analogy to the Ni2Zn11 parent γ-brass that is based on the 26-atom cluster, consisting of inner tetrahedron (IT), outer tetrahedron (OT), octahedron (OH), and cuboctahedron (CO). The refined site occupancies of the MnxNi2Zn11-x (x = 0.3, 0.5) reveal that the cluster center, which is empty in the Ni2Zn11, shows a partial occupation by Zn, with a partial depletion of Zn at the IT sites. The OH sites show a mixed Zn/Mn occupation. The OT and CO sites remain intact with respect to Ni2Zn11. Magnetic properties were studied for the Mn0.3Ni2Zn10.7 composition. The temperature-dependent zero-field-cooled and field-cooled magnetization, the ac susceptibility, the M(H) hysteresis curves, the thermoremanent magnetization, and the memory effect demonstrate typical broken-ergodicity phenomena of a magnetically frustrated spin system below the spin freezing temperature Tf ≈ 16 K. The Mn0.3Ni2Zn10.7 γ-brass phase classifies as a spin glass, originating predominantly from the random distribution of diluted Mn moments on the octahedral partial structure.

Structure and Superconductivity of Tin-Containing HfTiZrSnM (M = Cu, Fe, Nb, Ni) Medium-Entropy and High-Entropy Alloys.

In an attempt to incorporate tin (Sn) into high-entropy alloys composed of refractory metals Hf, Nb, Ti and Zr with the addition of 3d transition metals Cu, Fe, and Ni, we synthesized a series of alloys in the system HfTiZrSnM (M = Cu, Fe, Nb, Ni). The alloys were characterized crystallographically, microstructurally, and compositionally, and their physical properties were determined, with the emphasis on superconductivity. All Sn-containing alloys are multi-phase mixtures of intermetallic compounds (in most cases four). A common feature of the alloys is a microstructure of large crystalline grains of a hexagonal (Hf, Ti, Zr)5Sn3 partially ordered phase embedded in a matrix that also contains many small inclusions. In the HfTiZrSnCu alloy, some Cu is also incorporated into the grains. Based on the electrical resistivity, specific heat, and magnetization measurements, a superconducting (SC) state was observed in the HfTiZr, HfTiZrSn, HfTiZrSnNi, and HfTiZrSnNb alloys. The HfTiZrSnFe alloy shows a partial SC transition, whereas the HfTiZrSnCu alloy is non-superconducting. All SC alloys are type II superconductors and belong to the Anderson class of "dirty" superconductors.