Fabrication of Graphene-Polyimide Nanocomposites with Superior Electrical Conductivity.

We report on the fabrication of a novel class of lightweight materials, polyimide-graphene nanocomposites (0.01-5 vol %), with tunable electrical conductivity. The graphene-polyimide nanocomposites exhibit an ultra-low graphene percolation threshold of 0.03 vol % and maximum dc conductivity of 0.94 S/cm, which we attribute to excellent dispersion, extraordinary electron transport in the well-dispersed graphene, high number density of graphene nanosheets, and the π-π interactions between the aromatic moieties of the polyimide and the carbon rings in graphene. The dc conductivity data are shown to follow the power-law dependence on the graphene volume fraction near the percolation threshold. The ac conductivity of the nanocomposites is accurately represented by the extended pair-approximation model. The exponent s of the approximation is estimated to be 0.45-0.61, indicating anomalous diffusion of charge particles and a fractal structure for the conducting phase, lending support to the percolation model. Low-temperature dc conductivity of the nanocomposites is well-approximated by the thermal fluctuation-induced tunneling. Wide-angle X-ray scattering and transmission electron microscopy were utilized to correlate the morphology with the electrical conductivity. The lack of maxima in X-ray indicates the loss of structural registry and short-range ordering.

Trade-off between the Mechanical Strength and Microwave Electrical Properties of Functionalized and Irradiated Carbon Nanotube Sheets.

Carbon nanotube (CNT) sheets represent a novel implementation of CNTs that enable the tailoring of electrical and mechanical properties for applications in the automotive and aerospace industries. Small molecule functionalization and postprocessing techniques, such as irradiation with high-energy particles, are methods that can enhance the mechanical properties of CNTs. However, the effect that these modifications have on the electrical conduction mechanisms has not been extensively explored. By characterizing the mechanical and electrical properties of multiwalled carbon nanotube (MWCNT) sheets with different functional groups and irradiation doses, we can expand our insights into the extent of the trade-off that exists between mechanical strength and electrical conductivity for commercially available CNT sheets. Such insights allow for the optimization of design pathways for engineering applications that require a balance of material property enhancements.

Increased tensile strength of carbon nanotube yarns and sheets through chemical modification and electron beam irradiation.

The inherent strength of individual carbon nanotubes (CNTs) offers considerable opportunity for the development of advanced, lightweight composite structures. Recent work in the fabrication and application of CNT forms such as yarns and sheets has addressed early nanocomposite limitations with respect to nanotube dispersion and loading and has pushed the technology toward structural composite applications. However, the high tensile strength of an individual CNT has not directly translated into that of sheets and yarns, where the bulk material strength is limited by intertube electrostatic attractions and slippage. The focus of this work was to assess postprocessing of CNT sheets and yarns to improve the macro-scale strength of these material forms. Both small-molecule functionalization and electron-beam irradiation were evaluated as means to enhance the tensile strength and Young's modulus of the bulk CNT materials. Mechanical testing revealed a 57% increase in tensile strength of CNT sheets upon functionalization compared with unfunctionalized sheets, while an additional 48% increase in tensile strength was observed when functionalized sheets were irradiated. Similarly, small-molecule functionalization increased tensile strength of yarn by up to 25%, whereas irradiation of the functionalized yarns pushed the tensile strength to 88% beyond that of the baseline yarn.

Highly conductive multifunctional graphene polycarbonate nanocomposites.

Graphene nanosheet-bisphenol A polycarbonate nanocomposites (0.027-2.2 vol %) prepared by both emulsion mixing and solution blending methods, followed by compression molding at 287 °C, exhibited dc electrical percolation threshold of ∼0.14 and ∼0.38 vol %, respectively. The conductivities of 2.2 vol % graphene nanocomposites were 0.512 and 0.226 S/cm for emulsion and solution mixing. The 1.1 and 2.2 vol % graphene nanocomposites exhibited frequency-independent behavior. Inherent conductivity, extremely high aspect ratio, and nanostructure directed assembly of the graphene using PC nanospheres are the main factors for excellent electrical properties of the nanocomposites. Dynamic tensile moduli of nanocomposites increased with increasing graphene in the nanocomposite. The glass transition temperatures were decreased with increasing graphene for the emulsion series. High-resolution electron microscopy (HR-TEM) and small-angle neutron scattering (SANS) showed isolated graphene with no connectivity path for insulating nanocomposites and connected nanoparticles for the conductive nanocomposites. A stacked disk model was used to obtain the average particle radius, average number of graphene layers per stack, and stack spacing by simulation of the experimental SANS data. Morphology studies indicated the presence of well-dispersed graphene and small graphene stacking with infusion of polycarbonate within the stacks.

Reinforced thermoplastic polyimide with dispersed functionalized single wall carbon nanotubes.

Molecular pi-complexes were formed from pristine HiPCO single- wall carbon nanotubes (SWCNTs) and 1-pyrene- N-(4-N'-(5-norbornene-2,3-dicarboxyimido)phenyl butanamide, 1. Polyimide films were prepared with these complexes as well as uncomplexed SWCNTs and the effects of nanoadditive addition on mechanical, thermal, and electrical properties of these films were evaluated. Although these properties were enhanced by both nanoadditives, larger increases in tensile strength and thermal and electrical conductivities were obtained when the SWCNT/1 complexes were used. At a loading level of 5.5 wt %, the T(g) of the polyimide increased from 169 to 197 degrees C and the storage modulus increased 20-fold (from 142 to 3045 MPa). The addition of 3.5 wt % SWCNT/1 complexes increased the tensile strength of the polyimide from 61.4 to 129 MPa; higher loading levels led to embrittlement and lower tensile strengths. The electrical conductivities (DC surface) of the polyimides increased to 1 x 10(-4) Scm(-1) (SWCNT/1 complexes loading level of 9 wt %). Details of the preparation of these complexes and their effects on polyimide film properties are discussed.