ABSTRACT
K2Ca2(SO4)3:Eu nanophosphor was synthesized by chemical coprecipitation method and annealed at different temperatures from 400 to 900 °C. The nanophosphor annealed at 600 °C showed cubic structure with crystallite size ~25 nm. TEM shows morphology of K2Ca2(SO4)3:Eu nanophosphor was in the form of nanorods having diameter ~20 nm and length of ~100-200 nm. These samples were irradiated with gamma radiation for the doses varying from 10 mGy to 10 kGy and their Thermoluminescence (TL) and continuous-wave optically stimulated luminescence (CW-OSL) have been studied. CW-OSL response was found to be maximal for the sample annealed at 600 °C. The TL glow curve of the nanophosphor apparently showed a major peak at around 160 °C accompanied by three low intensity peaks at ~75, 215 and 285 °C. The traps responsible for all the TL peaks in K2Ca2(SO4)3:Eu were also found to be OSL sensitive. The qualitative correlation between TL peaks and CW-OSL response suggested that the traps associated with low temperature peaks are responsible for fast decay and the traps associated with the higher temperature peaks are responsible for slow decay of the OSL signal. OSL response showed linear behavior up to 1 kGy and saturated with further increase in the gamma dose. The wide OSL response makes studied K2Ca2(SO4)3:Eu nanophosphor a good candidate for high dose measurement.
ABSTRACT
A new Cu,P-doped, sodium fluorosilicate-based optically stimulated luminescence (OSL) phosphor is developed. This phosphor shows good OSL properties, and the sensitivity is comparable with that of the commercial Al(2)O(3):C (Landauer, Inc.) phosphor. For the luminescence averaged over initial 1 s, blue-stimulated luminescence and green-stimulated luminescence sensitivities were found to be 0.76 and 3.8 times, respectively, of Al(2)O(3):C (Landauer, Inc.) with 28 % of post-irradiation fading in 3 days and nil thereafter. The simple preparation procedure, fast decay, very good sensitivity and moderate fading will make this phosphor suitable for radiation dosimetry, using OSL.