ABSTRACT
Additively manufactured Ti scaffolds have been used for bone replacement and orthopaedic applications. In these applications, both morphological and mechanical properties are important for their in vivo performance. Additively manufactured Ti6Al4V triply periodic minimal surface (TPMS) scaffolds with diamond and gyroid structures are known to have high stiffness and high osseointegration properties, respectively. However, morphological deviations between the as-designed and as-built types of these scaffolds have not been studied before. In this study, the morphological and mechanical properties of diamond and gyroid scaffolds at macro and microscales were examined. The results demonstrated that the mean printed strut thickness was greater than the designed target value. For diamond scaffolds, the deviation increased from 7.5 µm (2.5% excess) for vertical struts to 105.4 µm (35.1% excess) for horizontal struts. For the gyroid design, the corresponding deviations were larger, ranging from 12.6 µm (4.2% excess) to 198.6 µm (66.2% excess). The mean printed pore size was less than the designed target value. For diamonds, the deviation of the mean pore size from the designed value increased from 33.1 µm (-3.0% excess) for vertical struts to 92.8 µm (-8.4% excess) for horizontal struts. The corresponding deviation for gyroids was larger, ranging from 23.8 µm (-3.0% excess) to 168.7 µm (-21.1% excess). Compressive Young's modulus of the bulk sample, gyroid and diamond scaffolds was calculated to be 35.8 GPa, 6.81 GPa and 7.59 GPa, respectively, via the global compression method. The corresponding yield strength of the samples was measured to be 1012, 108 and 134 MPa. Average microhardness and Young's modulus from α and ß phases of Ti6Al4V from scaffold struts were calculated to be 4.1 GPa and 131 GPa, respectively. The extracted morphology and mechanical properties in this study could help understand the deviation between the as-design and as-built matrices, which could help develop a design compensation strategy before the fabrication of the scaffolds.
ABSTRACT
Free-standing cantilevers, which directly translate specific biochemical reactions into micromechanical motion, have recently attracted much attention as label-free biosensors and micro/nano robotic devices. To exploit this mechanochemical sensing technology, it is essential to develop a fundamental understanding of the origins of surface stress. Here we report a detailed study into the molecular basis of stress generation in aqueous environments focusing on the pH titration of model mercaptohexadecanoic acid self-assembled monolayers (SAMs), using in situ reference cantilevers coated with nonionizable hexadecanethiol SAMs. Semiautomated data analysis and a statistical model were developed to quantify cyclic deprotonation/protonation reactions on multiple arrays. In-plane force titrations were found to have the sensitivity to detect ionic hydrogen bond formation between protonated and nonprotonated carboxylic acid groups in the proximity of the surface pK1/2, which generated a mean tensile differential surface stress of +1.2 +/- 0.3 mN/m at pH 6.0, corresponding to 1 pN attractive force between two adjacent MHA molecules. Conversely, the magnitude of compressive differential surface stress was found to increase progressively with pH >/= 7.0, reaching a maximum of -14.5 +/- 0.5 mN/m at pH 9.0, attributed to enhanced electrostatic repulsion between deprotonated carboxylic acid groups. However, striking differences were observed in the micromechanical responses to different ionic strength and ion species present in the aqueous environment, highlighting the critical role of counter- and co-ions on surface stress. Our findings provide fundamental insights into the molecular mechanisms of in-plane mechanochemistry, which may be exploited for biosensing and nanoactuation applications.
