ABSTRACT
Iron oxide nanoflowers (IONF) are densely packed multi-core aggregates known for their high saturation magnetization and initial susceptibility, as well as low remanence and coercive field. This study reports on how the local magnetic texture originating at the crystalline correlations among the cores determines the special magnetic properties of individual IONF over a wide size range from 40 to 400 nm. Regardless of this significant size variation in the aggregates, all samples exhibit a consistent crystalline correlation that extends well beyond the IONF cores. Furthermore, a nearly zero remnant magnetization, together with the presence of a persistently blocked state, and almost temperature-independent field-cooled magnetization, support the existence of a 3D magnetic texture throughout the IONF. This is confirmed by magnetic transmission X-ray microscopy images of tens of individual IONF, showing, in all cases, a nearly demagnetized state caused by the vorticity of the magnetic texture. Micromagnetic simulations agree well with these experimental findings, showing that the interplay between the inter-core direct exchange coupling and the demagnetizing field is responsible for the highly vortex-like spin configuration that stabilizes at low magnetic fields and appears to have partial topological protection. Overall, this comprehensive study provides valuable insights into the impact of crystalline texture on the magnetic properties of IONF over a wide size range, offering a deeper understanding of their potential applications in fields such as biomedicine and water remediation.
ABSTRACT
The present study describes the preparation of 50.3 nm superparamagnetic nanosorbents with high surface area for the adsorptive removal of lead and methyl orange from water. This material is based on the surface modification of iron oxide superparamagnetic nanoparticles with a double-shell coating of mesoporous silica whose porosity was increased up to 570 m2/g by the addition of a porogenic material and its calcination. The adsorptive performance of the nanosorbent was evaluated as a function of several parameters (e.g. solution pH, pollutant initial concentration, and contact time), concluding that pHs around 5 are needed to avoid precipitation of Pb2+ as Pb(OH)2 and the equilibrium adsorption capacity is reached after 2 h in all cases. The experimental data on the adsorption capacity of lead and methyl orange onto the nanosorbent were fit to a pseudo-second order kinetic model and Langmuir isotherm model. The maximum adsorption capacity value increases from 35 up to 50 mg/gNS for lead removal with increasing nanosorbent surface area. Contrary, for methyl orange the maximum adsorption goes up to 240 mg/gNS, indicating a larger nanosorbent surface affinity for the organic matter that is able to diffuse through the silica pores as probed by the intraparticle diffusion model. In addition, we found an good reusability (100% recovering after 4 sorption/desorption cycles for methyl orange removal), which makes of this magnetic nanosorbent suitable for remediation technologies.