ABSTRACT
Novel behavior has been observed at the interface of LaAlO3/SrTiO3 heterostructures such as two dimensional metallic conductivity, magnetic scattering and superconductivity. However, both the origins and quantification of such behavior have been complicated due to an interplay of mechanical, chemical and electronic factors. Here chemical and strain profiles near the interface of LaAlO3/SrTiO3 heterostructures are correlated. Conductive and insulating samples have been processed, with thicknesses respectively above and below the commonly admitted conductivity threshold. The intermixing and structural distortions within the crystal lattice have been quantitatively measured near the interface with a depth resolution of unit cell size. A strong link between intermixing and structural distortions at such interfaces is highlighted: intermixing was more pronounced in the hetero-couple with conductive interface, whereas in-plane compressive strains extended deeper within the substrate of the hetero-couple with the insulating interface. This allows a better understanding of the interface local mechanisms leading to the conductivity.
ABSTRACT
A reply to the comment by A. Yu. Kuntsevich and V. M. Pudalov.
ABSTRACT
We present the transport and capacitance measurements of 10 nm wide GaAs quantum wells with hole densities around the critical point of the 2D metal-insulator transition (critical density p(c) down to 0.8 × 10(10)/cm2, r(s) â¼ 36). For metallic hole density p(c) < p < p(c) + 0.15 × 10(10)/cm2, a reentrant insulating phase (RIP) is observed between the ν = 1 quantum Hall state and the zero-field metallic state and it is attributed to the formation of pinned Wigner crystal. Through studying the evolution of the RIP versus 2D hole density, we show that the RIP is incompressible and continuously connected to the zero-field insulator, suggesting a similar origin for these two phases.
ABSTRACT
We have studied the temperature dependent phonon emission rate P(T) of a strongly interacting (r(s) > or =22) dilute 2D GaAs hole system using a standard carrier heating technique. In the still poorly understood metallic state, we observe that P(T) changes from P(T) approximately T5 to P(T) approximately T7 above 100 mK, indicating a crossover from screened piezoelectric (PZ) coupling to screened deformation potential (DP) coupling for hole-phonon scattering. Quantitative comparison with theory shows that the long range PZ coupling between holes and phonons has the expected magnitude; however, in the metallic state, the short range DP coupling between holes and phonons is almost 20 times stronger than expected from theory. The density dependence of P(T) shows that it is easier to cool low-density 2D holes in GaAs than higher density 2D hole systems.
ABSTRACT
We report the temperature (T) and perpendicular magnetic-field (B) dependence of the Hall resistivity rho(xy)(B) of dilute metallic 2D holes in GaAs over a broad range of temperature (0.02-1.25 K). The low B Hall coefficient, R(H), is found to be enhanced when T decreases. Strong magnetic fields further enhance the slope of rho(xy)(B) at all temperatures studied. Coulomb interaction corrections of a Fermi liquid (FL) in the ballistic regime can not explain the enhancement of rho(xy) which occurs in the same regime as the anomalous metallic longitudinal conductivity. In particular, although the metallic conductivity in 2D systems has been attributed to electron interactions in a FL, these same interactions should reduce, not enhance, the slope of rho(xy)(B) as T decreases and/or B increases.