ABSTRACT
In this study, crumpled graphene oxide balls (CGBs) were prepared via capillary compression using a rapidly evaporating aerosol droplet method. The CGBs were observed using scanning electron microscopy (SEM), high-resolution transmission electron microscopy (HRTEM), and Raman spectroscopy. The size distributions of crumpled particles were obtained using a laser nanometer particle size analyzer (DLS). The dispersibility of the water and the ionic liquid (IL) was tested by ultrasonic dispersion. The tribological properties of water or ionic liquids containing crumpled graphene oxide ball additives (W/IL-CGB) were tested by a reciprocating friction tester and compared with water/ionic liquids with graphene oxide. The morphology of the wear scar was observed by a three-dimensional optical microscope and its lubrication mechanism was analyzed. The results show that the CGBs were successfully prepared by rapid evaporation of aerosol droplets, and the obtained CGBs were crumpled paper spheres. The CGBs had good water dispersion and ionic liquid dispersion, and IL-CGB has excellent anti-friction and anti-wear effects on steel-steel friction pairs. During the friction process, the CGB was adsorbed at the interface of the steel-steel friction pair to form a protective layer, which avoids the direct contact of the friction pair, thereby reducing friction and wear.
ABSTRACT
In this study, fluorographene nanosheets (FG nanosheets) were prepared via the solvent-ultrasonic exfoliation method. The fluorographene sheets were observed using field-emission scanning electron microscopy (FE-SEM). The microstructure of the as-prepared FG nanosheets was characterized by X-ray diffraction (XRD) and a thermal analyzer (TG). The tribological properties of FG nanosheets as an additive in ionic liquids in high vacuum were compared to that of ionic liquid (IL) with graphene (IL-G). The wear surfaces and transfer films were analyzed via an optical microscope, Raman spectroscopy, scanning electron microscopy (SEM), and X-ray photoelectron spectroscopy (XPS). The results show that FG nanosheets can be obtained from the simple solvent-ultrasonic exfoliation method. The prepared G nanosheets are a sheet, and the longer the ultrasonic time is, the thinner the sheet is. Ionic liquids with FG nanosheets had low friction and a low wear rate under high vacuum conditions. The improved frictional properties were attributed to the transfer film of FG nanosheets and more formation film of Fe-F.