ABSTRACT
Alkali halides such as calcium fluoride all have color center defects that absorb light in the visible region. Using a moncochromator equipped, aberration corrected, scanning transmission electron microscope (STEM) we recorded spectra showing the time evolution of the generation of F and H centers in calcium fluoride. The final stage of electron beam irradiation is the formation of metallic calcium nanoparticles. High resolution low loss spectra for the Vacuum Ultraviolet region were also recorded.
ABSTRACT
A novel carbon nitride compound, structurally related to the proposed graphitic phase of C(3)N(4), has been synthesized in a bulk well-crystallized form. The new material, with stoichiometry C(6)N(9)H(4)Cl, was prepared through a solid-state reaction of 2,4,6-triamino-1,3,5-triazine with 2,4,6-trichloro-1,3,5-triazine at 1.0-1.5 GPa and 500-550 degrees C and also through a self-reaction of 2-amino-4,6-dichloro-1,3,5-triazine at similar conditions. X-ray and electron diffraction measurements on the yellowish compound indicate a hexagonal space group (P6(3)/m) with cell parameters of a = 8.4379(10) A and c = 6.4296(2) A. This new compound possesses a two-dimensional C(6)N(9)H(3) framework that is structurally related to the hypothetical P6m2 graphitic phase of C(3)N(4), but with an ordered arrangement of C(3)N(3) voids. The large voids in the graphene sheets are occupied by chloride ions with an equivalent number of nitrogen atoms on the framework protonated for charge balance. The composition of the sample was determined by bulk chemical analysis and confirmed by electron energy loss (EELS) spectroscopy. The chemical and structural model is consistent with bulk density measurements and with the infrared and (13)C NMR spectra. This work represents the first bulk synthesis of a well-characterized and highly crystalline material containing a continuous network of alternating carbon and nitrogen atoms.