ABSTRACT
This study investigates the effect of extrusion screw speed and carbon nanotube (CNT) concentration on the thermal, mechanical, and electromagnetic interference shielding effectiveness (EMI SE) properties of Polycarbonate (PC)/acrylonitrile-butadiene-styrene (ABS) and its polymer nanocomposites (PNCs) by means of design of experiments (DoE) approach. A masterbatch method was employed to obtain the best dispersion of the CNTs throughout the polymer matrix. This study evaluates the thermo-mechanical characterisation of the polymers and PNCs at varying screw speeds to assess filler matrix bonding. The results highlight that CNT concentration has a significant effect on all mechanical properties, while screw speed only affects the Charpy impact strength and flexural properties of the samples. Compounding at 200 rpm has the best flexural and tensile strength, which is attributed to the best filler matrix bonding (highest storage modulus) of the PNCs. The best EMI SE results were obtained at 10 wt.% CNTs. This research contributes valuable insights into the effect of CNT concentration and extrusion screw speed on the mechanical, thermal and EMI SE properties of PC/ABS and its PNCs.
ABSTRACT
Biodegradable polyesters are a popular choice for both packaging and medical device manufacture owing to their ability to break down into harmless components once they have completed their function. However, commonly used polyesters such as poly(hydroxybutyrate) (PHB), poly(lactic acid) (PLA), and polycaprolactone (PCL), while readily available and have a relatively low price compared to other biodegradable polyesters, do not meet the degradation profiles required for many applications. As such, this study aimed to determine if the mechanical and degradation properties of biodegradable polymers could be tailored by blending different polymers. The seawater degradation mechanisms were evaluated, revealing surface erosion and bulk degradation in the blends. The extent of degradation was found to be dependent on the specific chemical composition of the polymer and the blend ratio, with degradation occurring via hydrolytic, enzymatic, oxidative, or physical pathways. PLA presents the highest tensile strength (67 MPa); the addition of PHB and PCL increased the flexibility of the samples; however, the tensile strength reduced to 25.5 and 18 MPa for the blends 30/50/20 and 50/25/25, respectively. Additionally, PCL presented weight loss of up to 10 wt.% and PHB of up to 6 wt.%; the seawater degradation in the blends occurs by bulk and surface erosion. The blending process facilitated the flexibility of the blends, enabling their use in diverse industrial applications such as medical devices and packaging. The proposed methodology produced biodegradable blends with tailored properties within a seawater environment. Additionally, further tests that fully track the biodegradation process should be put in place; incorporating compatibilizers might promote the miscibility of different polymers, improving their mechanical properties and biodegradability.
ABSTRACT
Hot melt extrusion offers an efficient way of increasing the solubility of a poorly soluble drug. Shellac has potential as a pharmaceutical matrix polymer that can be used in this extrusion process, with further advantages for use in enteric drug delivery systems. The rheological property of a material affects the extrusion process conditions. However, the literature does not refer to any published work that investigates the processability of various shellac materials. This work explores various types of shellac and explores their physicochemical and thermal properties along with their processability in the hot melt extrusion application. Physicochemical characterization of the materials was achieved using differential scanning calorimetry, Fourier transform infrared spectroscopy, scanning electron microscopy and energy-dispersive X-ray spectroscopy. Additional processability characterization was achieved using melt flow index and rheology analysis. The results indicated that there was no chemical difference between the various shellac types compared in this study. However, the extrudable temperature ranges and rheological properties of different shellac types varied; SSB 55 Pharma FL had the lowest processing temperature and glass transition temperatures. Due to the shear-thinning behaviours, shellac can be extruded at lower temperatures. This study provides necessary data to determine the processing conditions in hot melt extrusion applications for the range of shellac materials.
ABSTRACT
Poly-l-lactic acid (PLLA) is one of the most common bioabsorbable materials in the medical device field. However, its use in load-bearing applications is limited due to its inferior mechanical properties when compared to many of the competing metal-based permanent and bioabsorbable materials. The objective of this study was to directly compare the influence of both annealing and biaxial expansion processes to improve the material properties of PLLA. Results showed that both annealing and biaxial expansion led to an overall increase in crystallinity and that the crystallites formed during both processes were in the α' and α forms. 2D-WAXS patterns showed that the preferred orientation of crystallites formed during annealing was parallel to the circumferential direction. While biaxial expansion resulted in orientation in both axial and circumferential directions, with relatively equal sized crystals in both directions, Da (112 Å) and Dc (97 Å). The expansion process had the most profound effect on mechanical performance, with a 65% increase in Young's modulus, a 45% increase in maximum tensile stress and an 18-fold increase in strain at maximum load. These results indicate that biaxially expanding PLLA at a temperature above Tcc is possible, due to the high strain rates associated with stretch blow moulding.
ABSTRACT
Biodegradable polymers play a crucial role in the medical device field, with a broad range of applications such as suturing, drug delivery, tissue engineering, scaffolding, orthopaedics, and fixation devices. Poly-l-lactic acid (PLLA) is one of the most commonly used and investigated biodegradable polymers. The objective of this study was to determine the influence low shear microbore extrusion exerts on the properties of high molecular weight PLLA for medical tubing applications. Results showed that even at low shear rates there was a considerable reduction in molecular weight (Mn = 7-18%) during processing, with a further loss (Mn 11%) associated with resin drying. An increase in melt residence time from ~4 mins to ~6 mins, translated into a 12% greater reduction in molecular weight. The degradation mechanism was determined to be thermal and resulted in a ~22-fold increase in residual monomer. The differences in molecular weight between both batches had no effect on the materials thermal or morphological properties. However, it did affect its mechanical properties, with a significant impact on tensile strength and modulus. Interestingly there was no effect on the elongational proprieties of the tubing. There was also an observed temperature-dependence of mechanical properties below the glass transition temperature.
ABSTRACT
Hot melt extrusion (HME) is considered an efficient technique in developing solid molecular dispersions, and has been demonstrated to provide sustained, modified and targeted drug delivery resulting in improved bioavailability. However, most commercial enteric or pH-responsive polymers are relatively difficult to process or have high Glass Transition Temperature (Tg) values, making their use with temperature-sensitive drugs, probiotics or biologics not viable. Shellac is a natural thermoplastic, and after a review of current literature on the pharmaceutical HME process, a possible gap in the knowledge of the use of shellac to produce dosage forms by means of HME was identified. This work explores the possibility of SSB® 55 pharmaceutical-grade shellac as a melt-extrudable encapsulation polymer to entrap freeze-dried probiotic powder and to determine bacterial cell viability post-processing. Well-defined strands were produced from the physical mixture of shellac and Biocare® Bifidobacterium Probiotic. FTIR clarified that there are no significant interactions between the probiotic and polymer. All of the samples demonstrated less than 5% degradation over 24 h at pH of both 1.2 and 6.8. At pH 7.4, both loaded samples gave a similar dissolution trend with complete degradation achieved after 10-11 h. Following five-month storage, 57.8% reduction in viability was observed.