ABSTRACT
Combining X-ray Absorption Fine Spectroscopy (XAFS) with Anomalous Small-Angle X-ray Scattering (ASAXS) determines the location of Cu2+ ions in silicoaluminophosphate (SAPO-5) frameworks prepared by hydrothermal crystallization or impregnation. As expected, for the hydrothermally prepared sample, incorporation in the SAPO-5 framework was observed. For the first time preferential location of Cu2+ ions at the inner and outer surfaces of the framework is determined. Temperature-Programmed Reduction (TPR) and X-ray Photoelectron Spectroscopy (XPS) investigations demonstrated that such Cu2+ is stable in an argon (Ar) atmosphere up to 550 °C and can only be reduced under a hydrogen atmosphere. In contrast, Cu2+ deposited by impregnation on the pure SAPO-5 framework can be easily reduced to Cu+ in an Ar atmosphere. At lower Cu amounts, mononuclear tetrahedrally coordinated Cu species were formed which are relatively stable in the monovalent form. In contrast, at higher Cu amounts, CuO particles were found which change easily between the mono- and bivalent species.
ABSTRACT
Co-components are a powerful tool to tune the performance of catalysts, but their nature and their impact on the catalysts is often controversially discussed. In this study X-ray absorption spectroscopy (XAS) was employed to elucidate the nature of co-components and their impact on the catalytic reaction. In anatase-supported Pd-based catalysts for the gas-phase acetoxylation of toluene, less noble co-components (e.g., Mn, Co, and Sb) spread over the support in their oxidic form and changed their valence state on stream. Incorporated atoms such as C or a small part of the Sb affect the electronic structure of Pd. For the noble Au, only a weak interaction with the support and Pd was observed during time on stream. Only XAS at the K-edges together with investigations of the Pd L-edge for a better understanding of the electronic structure, supplemented by STEM for elemental mapping, allow such detailed insights.