In Vitro Performance of Bioinspired Phenolic Nanocoatings for Endosseous Implant Applications.

In the quest for finding new strategies to enhance tissue integration and to reduce the risk of bacterial colonization around endosseous implants, we report the application of auto-oxidative phenolic coatings made of tannic acid and pyrogallol to titanium surfaces. The functionalized surfaces were screened for their biological performance using cultures of primary human osteoblasts and biofilm-forming bioluminescent staphylococci S. epidermidis Xen43 and S. aureus Xen29. No toxic effect of the coatings on osteoblasts was detected. While tannic acid coatings seemed to induce a delay in osteoblast maturation, they revealed anti-inflammatory potential. Similar effects were observed for pyrogallol coatings deposited for 24 h. Thin pyrogallol coatings deposited for 2 h seemed to promote osteoblast maturation and revealed increased calcium deposition. The effects on osteoblast were found to be related to the release of phenolic compounds from the surfaces. While the phenolic coatings could not inhibit staphylococcal biofilm formation on the titanium surfaces, released phenolic compounds had an inhibitory effect the growth of planktonic bacteria. In conclusion, the assessed coating systems represent a versatile functionalization method which exhibit promising effects for endosseous implant applications.

Deposition Kinetics of Bioinspired Phenolic Coatings on Titanium Surfaces.

Polyphenols can form functional coatings on a variety of different materials through auto-oxidative surface polymerization in a manner similar to polydopamine coatings. However, the mechanisms behind the coating deposition are poorly understood. We report the coating deposition kinetics of the polyphenol tannic acid (TA) and the simple phenolic compound pyrogallol (PG) on titanium surfaces. The coating deposition was followed in real time over a period of 24 h using a quartz crystal microbalance with dissipation monitoring (QCM-D). TA coatings revealed a multiphasic layer formation: the deposition of an initial rigid layer was followed by the buildup of an increasingly dissipative layer, before mass adsorption stopped after approximately 5 h of coating time. The PG deposition was biphasic, starting with the adsorption of a nonrigid viscoelastic layer which was followed by layer stiffening upon further mass adsorption. Coating evaluation by ellipsometry and AFM confirmed the deposition kinetics determined by QCM-D and revealed maximum coating thicknesses of approximately 50 and 75 nm for TA and PG, respectively. Chemical characterization of the coatings and polymerized polyphenol particles indicated the involvement of both physical and chemical interactions in the auto-oxidation reactions.

Effect of cathodic polarization on coating doxycycline on titanium surfaces.

Cathodic polarization has been reported to enhance the ability of titanium based implant materials to interact with biomolecules by forming titanium hydride at the outermost surface layer. Although this hydride layer has recently been suggested to allow the immobilization of the broad spectrum antibiotic doxycycline on titanium surfaces, the involvement of hydride in binding the biomolecule onto titanium remains poorly understood. To gain better understanding of the influence this immobilization process has on titanium surfaces, mirror-polished commercially pure titanium surfaces were cathodically polarized in the presence of doxycycline and the modified surfaces were thoroughly characterized using atomic force microscopy, electron microscopy, secondary ion mass spectrometry, and angle-resolved X-ray spectroscopy. We demonstrated that no hydride was created during the polarization process. Doxycycline was found to be attached to an oxide layer that was modified during the electrochemical process. A bacterial assay using bioluminescent Staphylococcus epidermidis Xen43 showed the ability of the coating to reduce bacterial colonization and planktonic bacterial growth.