ABSTRACT
Resistance spot welding (RSW) is one of the most effective welding methods for titanium alloys, in particular Ti-6Al-4V. Ti-6Al-4V is one of the most used materials with its good ductility, high strength, weldability, corrosion resistance, and heat resistance. RSW and Ti-6Al-4V materials are often widely used in industrial manufacturing, particularly in automotive and aerospace industries. To understand the phenomenon of resistance spot weld quality, the physical and mechanical properties of Ti-6Al-4V spot weld are essential to be analyzed. In this study, an experiment was conducted using the Taguchi L9 method to find out the optimum level of the weld joint strength. The given optimum level sample was analyzed to study the most significant affecting RSW parameter, the failure mode, the weld nugget microstructure, and hardness values. The high heat input significantly affect the weld nugget temperature to reach and beyond the ß-transus temperature. It led to an increase in the weld nugget diameter and the indentation depth. The expulsion appeared in the high heat input and decreased the weld nugget strength. It was caused by the molten material ejection in the fusion zone. The combination of high heat input and rapid air cooling at room temperature generated a martensite microstructure in the fusion zone. It increased the hardness, strength, and brittleness but decreased the ductility.
ABSTRACT
Welding parameters obviously determine the joint quality during the resistance spot welding process. This study aimed to investigate the effect of welding current and electrode force on the heat input and the physical and mechanical properties of a SS316L and Ti6Al4V joint with an aluminum interlayer. The weld current values used in this study were 11, 12, and 13 kA, while the electrode force values were 3, 4, and 5 kN. Welding time and holding time remained constant at 30 cycles. The study revealed that, as the welding current and electrode force increased, the generated heat input increased significantly. The highest tensile-shear load was recorded at 8.71 kN using 11 kA of weld current and 3 kN of electrode force. The physical properties examined the formation of a brittle fracture and several weld defects on the high current welded joint. The increase in weld current also increased the weld diameter. The microstructure analysis revealed no phase transformation on the SS316L interface; instead, the significant grain growth occurred. The phase transformation has occurred on the Ti6Al4V interface. The intermetallic compound layer was also investigated in detail using the EDX (Energy Dispersive X-Ray) and XRD (X-Ray Diffraction) analyses. It was also found that both stainless steel and titanium alloy have their own fusion zone, which is indicated by the highest microhardness value.
ABSTRACT
Micro-turning is a micro-mechanical cutting method used to produce small diameter cylindrical parts. Since the diameter of the part is usually small, it may be a little difficult to improve the surface quality by a second operation, such as grinding. Therefore, it is important to obtain the good surface finish in micro turning process using the ideal cutting parameters. Here, the multi-objective optimization of micro-turning process parameters such as cutting speed, feed rate and depth of cut were performed by response surface method (RSM). Two important machining indices, such as surface roughness and material removal rate, were simultaneously optimized in the micro-turning of a Ti6Al4V alloy. Further, the scanning electron microscope (SEM) analysis was done on the cutting tools. The overall results depict that the feed rate is the prominent factor that significantly affects the responses in micro-turning operation. Moreover, the SEM results confirmed that abrasion and crater wear mechanism were observed during the micro-turning of a Ti6Al4V alloy.
ABSTRACT
Porous metal structures have emerged as a promising solution in repairing and replacing damaged bone in biomedical applications. With the advent of additive manufacturing technology, fabrication of porous scaffold architecture of different unit cell types with desired parameters can replicate the biomechanical properties of the natural bone, thereby overcoming the issues, such as stress shielding effect, to avoid implant failure. The purpose of this research was to investigate the influence of cube and gyroid unit cell types, with pore size ranging from 300 to 600 µm, on porosity and mechanical behavior of titanium alloy (Ti6Al4V) scaffolds. Scaffold samples were modeled and analyzed using finite element analysis (FEA) following the ISO standard (ISO 13314). Selective laser melting (SLM) process was used to manufacture five samples of each type. Morphological characterization of samples was performed through micro CT Scan system and the samples were later subjected to compression testing to assess the mechanical behavior of scaffolds. Numerical and experimental analysis of samples show porosity greater than 50% for all types, which is in agreement with desired porosity range of natural bone. Mechanical properties of samples depict that values of elastic modulus and yield strength decreases with increase in porosity, with elastic modulus reduced up to 3 GPa and yield strength decreased to 7 MPa. However, while comparing with natural bone properties, only cube and gyroid structure with pore size 300 µm falls under the category of giving similar properties to that of natural bone. Analysis of porous scaffolds show promising results for application in orthopedic implants. Application of optimum scaffold structures to implants can reduce the premature failure of implants and increase the reliability of prosthetics.